Ardalani A, Naffakh-Moosavy H. Brazing of 17-4 PH stainless steel to Ti-6Al-4V alloy using BNi-2 filler metal. JWSTI 2024; 9 (2) :103-113
URL: http://jwsti.iut.ac.ir/article-1-446-en.html
1- Material Engineering, Tarbiat Modares University, Tehran, Iran.
2- Material Engineering, Tarbiat Modares University, Tehran, Iran. , h.naffakh-moosavy@modares.ac.ir
Abstract:   (761 Views)
In this research, the effect of temperature and time parameters are investigated on the microstructure and mechanical properties of  dissimilar brazing of 17-4 PH stainless steel and Ti-6Al-4V alloy with BNi-2 filler metal. The microstructure of the joint is evaluated with optical and scanning electron microscopes and the mechanical properties of the joint are also evaluated with tensile-shear and microhardness tests. It can be seen that at a constant temperature of 1050°C, increasing the time from 15 to 30 minutes decreases the shear strength from 34.66 to 29.39 MPa. Formation of brittle intermetallic compounds like NiTi2 and FeTi2 increase strength and promote brittle fracture.At a fixed time of 15 minutes, increasing the temperature from 1050 to 1100 °C causes the strength to increase from 34.66 to 38.46 MPa. Also, the increase in temperature and time increases the ISZ thickness formed in the joints on the side of the filler metal - Ti-6Al-4V from 41.40 to 81.48 microns. The increase in temperature and time also causes more diffusion of boron into the SS-filler joint, which forms various boron compounds and widens this region.
Full-Text [PDF 5087 kb]   (277 Downloads)    
Type of Study: Research | Subject: Special

Add your comments about this article : Your username or Email:
CAPTCHA

Send email to the article author


Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2024 CC BY-NC 4.0 | Journal of Welding Science and Technology of Iran

Designed & Developed by : Yektaweb