Volume 8, Issue 2 (Journal OF Welding Science and Technology 2023)                   JWSTI 2023, 8(2): 13-21 | Back to browse issues page

XML Persian Abstract Print


Download citation:
BibTeX | RIS | EndNote | Medlars | ProCite | Reference Manager | RefWorks
Send citation to:

Pourjafar A, dehmolaei R, Alavi zaree R, Ranjbar K, Tavakoli Shoushtari M. Effect of diffusion bonding temperature on microstructure properties of Zr/Ti interlayer in the diffusion bonded joints of Zr702 to A516 steel. JWSTI 2023; 8 (2) :13-21
URL: http://jwsti.iut.ac.ir/article-1-403-en.html
1- Department of Materials Science & Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz, Ahvaz, Iran
2- Department of Materials Science & Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz, Ahvaz, Iran , dehmolaei@scu.ac.ir
Abstract:   (2046 Views)
In this study, the effect of temperature on the microstructure and reactive layer at the interface between the Ti interlayer and the base metal related to the diffusion bonding of Zr702 to A516 low alloy steel was investigated. The joining was done using the spark plasma sintering technique at temperatures of 900, 950 and 1000°C for 30 minutes. Field Emission Scanning Electron Microscope (FESEM) equipped with EDS analysis was used to investigate the microstructure of the interfaces in various joints. Investigations showed that at all temperatures, with the diffusion of atoms and the formation of a reactive layer between the Ti interlayer and Zr702, no intermetallic phases, cracks, porosity and discontinuities were formed at their interfaces. . It was found that increasing the bonding temperature did not cause the formation of new phases and compounds in the interface and only increased the thickness of the reaction layer. The measurement of the thickness of the reactive layer showed that the maximum and minimum amounts of diffusion were 84 microns at 1000 °C and 64 microns at 900 °C respectively
Full-Text [PDF 2944 kb]   (1400 Downloads)    
Type of Study: Research | Subject: Special

Add your comments about this article : Your username or Email:
CAPTCHA

Send email to the article author


Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2024 CC BY-NC 4.0 | Journal of Welding Science and Technology of Iran

Designed & Developed by : Yektaweb