Volume 5, Issue 2 ((Journal OF Welding Science and Technology) 2020)                   JWSTI 2020, 5(2): 123-134 | Back to browse issues page

XML Persian Abstract Print


Abstract:   (4076 Views)
In this study, corrosion behavior of Ti-6Al-4V titanium alloy joint by friction stir welding with a rotational speed of 375 rpm and a travel speed of 100 mm/min was investigated. The welding procedure was carried out under β-transus temperature that was consisted of equiaxed grains in the stir zone. The corrosion behavior of the welded joint was investigated in 3.5% NaCl solution at temperatures of 25, 37 and 80 . Microstructure investigation of sample surfaces after electrochemical experiments was conducted using SEM. results revealed that the β phase was mainly corroded at all three testing temperatures, however the corrosion in the sample tested at 80 °C was more considerable.
Full-Text [PDF 4648 kb]   (1291 Downloads)    

Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.