Nikbakht1 H, Khanzadeh M, Bakhtiari H. Investigation of the effect of explosive welding variables on the corrosion behavior of the joint of two explosive layers of 5000 series copper-copper sheets. JWSTI 2022; 7 (2) :13-24
URL: http://jwsti.iut.ac.ir/article-1-377-en.html
Investigation of the effect of explosive welding variables on the corrosion behavior of the joint of two explosive layers of 5000 series copper-copper sheets
Homan Nikbakht1 , Mohammadreza Khanzadeh * 1, Hamid Bakhtiari
1- , khanzadeh@iaumajlesi.ac.ir
Abstract:   (2284 Views)
In the present study, the corrosion behavior and microstructural changes of 5000 series aluminum and copper sheets after the explosive welding process have been investigated. Explosive welding is performed with a fixed stop interval and change of explosive load. Dynamic potential polarization tests and electrochemical impedance spectroscopy, light microscopy, and scanning electron microscopy were used. The results of TOEFL polarization curves show that the lowest corrosion velocity was related to the sample with an explosive load of 1.5 and the highest corrosion velocity was related to the sample with an explosive load of 2.5. The corrosion resistance of a sample with an explosive load of 2.5 is less than that of a sample with an explosive load of 1.5 due to more severe plastic deformation at the joint. The metallographic results show a wave-vortexing of the joint due to the increase in the explosive charge. The results of the impedance test in welded samples showed that the value of n (experimental power parameter) decreased with wave-vortexing of the joint and the sample with 2.5 explosive load had the highest corrosion rate. Based on the results of scanning electron microscopy, it was observed that with an increasing explosive charge, the thickness of the local melting layer gradually increases.
Keywords: Explosive welding, explosive ratio, severe plastic deformation, vortex.
Full-Text [PDF 2481 kb]   (705 Downloads)    
Type of Study: Research | Subject: Special
Add your comments about this article : Your username or Email:
CAPTCHA
Send email to the article author

Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2024 CC BY-NC 4.0 | Journal of Welding Science and Technology of Iran

Designed & Developed by : Yektaweb