Volume 3, Issue 1 (Journal OF Welding Science and Technology of Iran 2017)                   JWSTI 2017, 3(1): 42-53 | Back to browse issues page

XML Persian Abstract Print


Download citation:
BibTeX | RIS | EndNote | Medlars | ProCite | Reference Manager | RefWorks
Send citation to:

Zohoori-Shoar V, Karimzadeh F, Eslami A. Evaluation of mechanical properties of nanostructured Al 6061 alloy weldment during resistance spot welding process. JWSTI 2017; 3 (1) :42-53
URL: http://jwsti.iut.ac.ir/article-1-140-en.html
1- Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran.
Abstract:   (10066 Views)
In this study, The Al 6061 alloy sheets were produced by Cryorolling process and then were welded by resistance spot welding method. In this regard, the solution treated Al 6061 alloy cryorolled subsequently up to 90% reduction in thickness to produce nanostructure alloy. The cryorolled sheets were then subjected to aging treatment (130˚C-30h) in order to obtain simultaneous strength and ductility. Tensile strength of 370 MPa, hardness of 135 HV, and ductility of 11 % was obtained for the nanostructured Aluminum sheets. The Cryorolled samples were then resistance spot welded with different welding parameters, including welding current 50 to 100 kA, electrode force of 2.8 kN, and welding time of 0.1 s. The most tensile shear peak load of weld spot of nanostructured samples was 5580 N. The results for different welded samples showed that the nanostructured ones, have higher weld strength when compared with 6061-T6 Aluminum alloy samples with common grain size.
Full-Text [PDF 111 kb]   (1621 Downloads)    
Type of Study: Research | Subject: Special

Add your comments about this article : Your username or Email:
CAPTCHA

Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.

© 2024 CC BY-NC 4.0 | Journal of Welding Science and Technology of Iran

Designed & Developed by : Yektaweb