@article{ 
author = {Borhani, M.R and Shoja-Razavi, S.R. and Kermani, F.},  
title = {The dissimilar joint of 316L austenitic stainless steel to 5083 aluminum alloy by friction stir welding and investigation of its microstructure and mechanical properties}, 
abstract ={In this study, the effects of friction stir welding (FSW) parameters on the properties of dissimilar joints formed between 5083 aluminum alloys and 316L austenitic stainless steel, with a thickness of 4 mm, are investigated. The tool speed is varied in the range of 16 to 25 mm/min, while the tool rotation speed is maintained at a constant value of 250 rpm. To examine the microstructure of different weld regions, both optical and scanning electron microscopes are employed. To assess the mechanical properties, hardness and tensile tests are conducted. The results shows the formation of a composite region characterized by steel reinforcement particles dispersed within an aluminum matrix. At the steel-aluminum interface, a single layer of discontinuous intermetallic composition with a thickness of approximately 2 micrometers is observed. Notably, when the rotation speed is set to 250 rpm and the tool speed is 16 mm/min, a tensile strength of 298 MPa and ductility of 26% (93% of the tensile strength and 50% of the ductility of the 5083 aluminum alloy) are achieved.},  
Keywords = {dissimilar joint, 316 austenitic stainless steel, 5083 aluminum alloy, friction stir welding, microstructure, mechanical properties..},
volume = {10},
Number = {1}, 
pages = {1-13}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {اتصال غیرمشابه فولاد زنگ‌نزن آستنیتی AISI316L به آلیاژ آلومینیوم 5083 به روش اصطکاکی اغتشاشی و بررسی ریزساختار و خواص مکانیکی آن},
abstract_fa ={در این پژوهش اثر پارامترهای جوشکاری اصطکاکی اغتشاشی (FSW) بر خصوصیات اتصال غیرهمجنس آلیاژهای آلومینیوم 5083 و فولاد زنگ‌نزن آستنیتی L316، به ضخامت 4 میلی‌متر بررسی شده است. سرعت پیشروی ابزار در محدوده 16 تا 25 میلی‌متر بر دقیقه و سرعت چرخش ابزار برابر با سرعت ثابت 250 دور بر دقیقه در نظر گرفته شد. جهت بررسی‌‌ ریزساختار مناطق مختلف جوش، میکروسکوپ‌های نوری و الکترونی روبشی و جهت بررسی خواص مکانیکی، آزمون‌‌های سختی و کشش انجام‌شد. نتایج، تشکیل یک منطقه کامپوزیتی متشکل از ذرات تقویت‌کننده فولادی در زمینه ریزدانه آلومینیوم در منطقه اغتشاشی را نشان‌داد. در فصل مشترک فولاد و آلیاژ آلومینیوم، یک‌لایه ترکیب بین فلزی ناپیوسته به ضخامت حدود 2 میکرومتر مشاهده شد؛ همچنین با انتخاب سرعت چرخش 250 دور بر دقیقه و سرعت پیشروی 16 میلی‌متر بر دقیقه، استحکام کششی برابر با 298 مگاپاسکال و انعطاف 26 درصد (93 درصد استحکام کششی و 50 درصد انعطاف‌پذیری آلیاژ آلومینیوم) به دست آمد.},
keywords_fa = {اتصال غیرهمجنس, فولاد زنگ‌نزن آستنیتی L316, آلیاژ آلومینیوم 5083, جوشکاری اصطکاکی اغتشاشی, ریزساختار, خواص مکانیکی.},

doi = { 10.47176/JWSTI.2024.14},
url = {http://jwsti.iut.ac.ir/article-1-437-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-437-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {Nazari, A. R. and Taherizadeh, A. and Atapour, M.},  
title = {Investigating microstructure and mechanical properties of dissimilar resistance spot welding of AISI 430 to S500 MC}, 
abstract ={In this study, the microstructure and mechanical properties of dissimilar resistance spot welding of AISI 430 steel and S500 MC steel were investigated. To carry out this research, Taguchi's L9 array was used to determine the number of samples and determine the range of variables of each sample, and after welding the samples and performing the shear tensile test, the sample with the highest tensile shear strength (13740 N) and the highest amount of fracture energy (102160 Joules), was considered as the best example; Also, the variables of this sample, i.e., welding current of 12 kW, welding time of 12 cycles, and electrode force of 3 kN, had the highest signal-to-noise values, and these values were chosen among the best range of variables among the proposed variables. Then, a microhardness test was performed on the welded sample with the above variables, and microstructural studies were performed by optical microscope and scanning electron microscope. The hardness of the weld zone was observed to be about 400 Vickers, and the microstructure of the weld metal consisted of ferrite, martensite, and Widmannstatten ferrite.},  
Keywords = {Resistance Spot Welding, AISI 430, S500 MC Steel.},
volume = {10},
Number = {1}, 
pages = {15-30}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {بررسی ریزساختار و خواص مکانیکی اتصال غیرمشابه به روش جوشکاری نقطه‌ای مقاومتی فولاد AISI 430 به فولاد خودرویی S500 MC},
abstract_fa ={در این مطالعه به بررسی ریزساختار و خواص مکانیکی اتصال غیرمشابه جوشکاری نقطه‌ای مقاومتی فولاد AISI 430 و فولاد S500 MC پرداخته شد. برای انجام این پژوهش از آرایه L9 تاگوچی برای مشخص شدن تعداد نمونه‌ها و تعیین محدوده متغیرهای هر نمونه استفاده شد و پس از جوشکاری نمونه‌ها و انجام آزمون کشش برشی، نمونه‌ای که دارای بیشترین استحکام کشش برشی(13740 نیوتن) و بیشترین مقدار انرژی شکست(102160ژول) بود، به عنوان بهترین نمونه در نظر گرفته شد؛ همچنین متغیرهای این نمونه یعنی جریان جوشکاری 12 کیلووات، زمان جوشکاری 12 سیکل و نیروی الکترود 3 کیلو نیوتن دارای بیشترین مقادیر سیگنال به نویز بودند و این مقادیر جز بهترین محدوده متغیرها در بین متغیرهای پیشنهادی انتخاب شدند. سپس بر روی نمونه جوشکاری شده با متغیرهای فوق، آزمون میکروسختی انجام شد و مطالعات ریزساختاری توسط میکروسکوپ نوری و میکروسکوپ الکترونی روبشی انجام شدند. سختی ناحیه جوش حدود 400 ویکرز مشاهده شد و ریزساختار فلزجوش از فریت، مارتنزیت و فریت ویدمن اشتاتن تشکیل شده بود.},
keywords_fa = {جوشکاری نقطه‌ای مقاومتی, فولاد AISI 430, فولاد S500 MC.},

doi = { 10.47176/JWSTI.2024.15},
url = {http://jwsti.iut.ac.ir/article-1-454-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-454-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {Adelian, A. and Ranjbar, Kh. and TavakoliShoushtari, M.R.},  
title = {The effect of double overaging treatment on the microstructure and pitting corrosion behavior of the weld zone in 17-4PH stainless steel}, 
abstract ={This research studied the effect of two-stage over aging treatment on the pitting corrosion behavior and microstructure of the weld metals in the 17-4 precipitation hardening stainless steel. For this purpose, this steel was subjected to solution annealing heat treatment at 1035°C for one hour before welding. Then gas tungsten arc welding (GTAW) was performed using ER630 similar filler metal. Subsequently, a section of the weldment was subjected to two-stage over aging treatment. The microstructure and corrosion resistance of the weld zone after the two-stage over aging treatment were investigated and compared with the weld zone behavior in the as-weld condition. Microstructural studies showed that the two-stage over aging treatment of the weld zone led to the tempering of the martensitic, the formation of more reversed austenite, and the formation of α-ferrite. The volume fraction of austenite in the as-weld condition was approximately %7 and increased to about %30 after two-stage over aging treatment, a four-fold increase. The pitting potential (EPit) of weld metal was -18.15 mv in the as-weld condition and reached 122.54 mv after two-stage over aging treatment, which also signifies an improvement in pitting resistance. The two-stage over aging treatment also reduced the potential differences between the different parts of welding zones reducing the galvanic corrosion occurrence. The assessment of mechanical properties through impact test revealed that impact resistance after two-stage over aging treatment can be increased by about %66 compared to as-weld condition.  },  
Keywords = {17-4PH Stainless Steel, GTA Welding, Heat Treatment, Overaging, Pitting Corrosion},
volume = {10},
Number = {1}, 
pages = {31-46}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {اثر عملیات حرارتی فراپیرسازی دو مرحله‌ای بر ریزساختار و رفتار خوردگی حفره‌ای ناحیه جوش فولاد زنگ‌نزن17-4PH},
abstract_fa ={هدف از انجام این پژوهش، بررسی تأثیر عملیات حرارتی فرا پیرسازی دو مرحله ای بر ریزساختار و رفتار خوردگی حفره‌ای ناحیه اتصال فولاد زنگ نزن 17-4PH می‌باشد. بدین منظور این فولاد پیش از جوشکاری تحت عملیات حرارتی آنیل انحلالی در دمای 1035 درجه سانتی‌گراد به مدت یک ساعت قرار گرفت. سپس جوشکاری قوس تنگستن-گاز (GTAW) به وسیله فلزپرکننده هم جنس ER630 انجام شد. پس از آن، بخشی از قطعه جوشکاری شده، تحت عملیات حرارتی فراپیرسازی دو مرحله ای قرار گرفت. ریزساختار و مقاومت به خوردگی ناحیه جوش، پس از عملیات فراپیرسازی دو مرحله‌ای، مورد بررسی و آزمون قرار گرفت و  با رفتار جوش در حالت as-weld مقایسه گردید. بررسی‌‌های ریزساختاری نشان داد که فراپیرسازی دو مرحله‌ای ناحیه جوش منجر به تمپر شدن ریزساختار مارتنزیتی و تشکیل آستنیت برگشتی بیشتر و نیز تشکیل فریت α گردید. کسر حجمی آستنیت موجود در فلزجوش در حالت as-weld از حدود %7 به حدود ۳۰% در حالت فراپیرسازی دو مرحله‌ای رسید که افزایش بیش از 4 برابری را نشان می‌دهد. در حالت as-weld پتانسیل حفره دار شدن (EPit) فلزجوش مقدار mv15/18- را نشان داد که در مقایسه با حالت فراپیرسازی دو مرحله‌ای با پتانسیلmv54/122، کاهش قابل توجه حساسیت به خوردگی حفره‌ای با انجام فراپیرسازی دو مرحله‌ای را نشان می‌دهد. همچنین عملیات حرارتی فراپیرسازی دو مرحله‌ای نشان داد که اختلاف پتانسیل‌های خوردگی نواحی مختلف جوش کاهش یافته که موجب کاهش خوردگی گالوانیکی می‌شود. ارزیابی رفتار مکانیکی توسط آزمون مقاومت به ضربه مشخص کرد که ناحیه جوش در حالت فراپیرسازی دو مرحله‌ای مقاومت به ضربه بیشتری نسبت به حالتas-weld داشته و افزایش۶۶ درصدی را نشان داد.  },
keywords_fa = {فولاد 17-4PH, جوشکاریGTAW, عملیات حرارتی, فراپیرسازی, خوردگی حفره‌ای.},

doi = { 10.47176/JWSTI.2024.16},
url = {http://jwsti.iut.ac.ir/article-1-456-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-456-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {Khorram, A. and Habibi, H. and Yazdipour, A.},  
title = {The effect of diffusion welding parameters on the microstructural characteristics and mechanical properties of dissimilar joint between AISI 418 stainless steel  and Inconel 738 superalloy using nickel interlayer}, 
abstract ={This study aimed to investigate the effect of diffusion welding parameters on the microstructural characteristics and mechanical properties of the dissimilar joint between AISI 418 stainless steel and Inconel 738 superalloy using Ni interlayer with a thickness of 50 µm. The experiments were performed in a vacuum furnace at three temperatures of 1000, 1050 and 1150 °C for 45, 60, 75 and 90 min under the pressure of 5 MPa.The results show that voids and non-bonded areas are seen in the samples that were bonded at a lower temperature (1000 °C). By increasing the joining temperature from 1000 °C to 1050 °C, all micro discontinuities have disappeared, which shows that the microplastic deformation of roughness has improved. Then, by increasing the temperature to 1150 °C,non-bonded areas are observed in the joint due to the reduction of pressure on the contact surfaces. When pure nickel is used as an interlayer, intermetallic compounds of γ' [Ni3(Al, Ti)] are formed in the γ matrix phase on the side of Inconel 738 superalloy while compounds of FeNi3 and γ (γFe, Ni) are formed on the side of AISI 418 stainless steel. According to the results of line scan analysis, the slope and penetration of elements in Inconel 738 superalloy is lower than AISI 418 stainless steel , which indicates less penetration in Inconel 738 superalloy. In the sample welded at the temperature of 1050 °C and the time of  90 Min, the penetration value of the nickel interlayer in AISI 418 stainless steel  and Inconel 738 superalloy was 40 µm and 35 µm, respectively. By comparing the maximum hardness, it can be concluded that the joint at the temperature of 1050 °C and the time of 90 Min has a lower maximum hardness than other samples. Therefore, it has better joint characteristics than other samples in terms of intermetallic compounds. The highest value of shear strength was obtained at the temperature of 1050 °C and the time of 90 Min, which is equal to 270 MPa.},  
Keywords = {Diffusion Welding, AISI 418 stainless steel , Inconel 738 alloy, Microstructure, Shear strength.},
volume = {10},
Number = {1}, 
pages = {47-64}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {تاثیر پارامترهای اتصال نفوذی بر ریزساختار و خواص مکانیکی اتصال غیرهمجنس فولاد زنگ‌نزن مارتنزیتی 418 به سوپرآلیاژ اینکونل 738 با استفاده از لایه واسط نیکل},
abstract_fa ={هدف از پژوهش حاضر بررسی تاثیر پارامترهای اتصال نفوذی بر ریزساختار و خواص مکانیکی اتصال فولاد مارتنزیتی 418 به سوپرآلیاژ اینکونل 738 با استفاده از لایه واسط نیکل خالص با ضخامت 50 میکرومتر می‌باشد. آزمایش‌ها در کوره خلاء در سه دمای 1050،1000 و 1150 درجه سانتی‌گراد برای مدت زمان‌ 45 ، 60 ، 75 و 90 دقیقه و تحت فشار 5 مگاپاسکال انجام پذیرفت. نتایج نشان می‌دهد که حفره‌ها و نواحی بدون پیوند در نمونه‌هایی‌که در دمای پایین‌تر (1000 درجه سانتی‌گراد) به هم متصل شده‌اند دیده می‌شوند. با افزایش دمای اتصال از 1000 درجه سانتی‌گراد به 1050 درجه سانتی‌گراد، تمام ناپیوستگی‌های میکرو از بین رفته‌اند که نشان می‌دهد تغییر شکل میکروپلاستیک زبری‌ها بهبود یافته است. سپس با افزایش دما به 1150 درجه سانتی‌گراد، نواحی بدون پیوند در اتصال مشاهده می‌شوند  که به علت کاهش فشار اعمالی از سوی فیکسچر بر روی سطوح در تماس به علت افزایش دما می‌باشد. هنگام استفاده از نیکل خالص به‌عنوان لایه واسط، در سمت سوپرآلیاژ اینکونل 738 ترکیباتی بین فلزی [γ' [Ni3Al, Ti در فاز زمینه γ تشکیل می‌شوند در حالی‌که در سمت فولاد مارتنزیتی418 ترکیبات مخلوط فازی FeNi3 و (γFe,Ni) γ تشکیل می‌شوند. با توجه به نتایج آنالیز اسکن خطی، شیب و نفوذ عناصر در سوپرآلیاژ اینکونل 738 کمتر از فولاد مارتنزیتی 418 می‌باشد که نشان دهنده‌ نفوذ کمتر در سوپرآلیاژ اینکونل 738 است. در نمونه جوشکاری شده در دمای1050 درجه سانتی‌گراد و زمان 90 دقیقه، میزان نفوذ لایه نیکل در فولاد مارتنزیتی 418 برابر 40 میکرومتر و در سوپرآلیاژ اینکونل 738 برابر 35 میکرومتر می‌باشد. با مقایسه بیشینه سختی می‌توان نتیجه گرفت اتصال در شرایط دمای 1050 درجه سانتی‌گراد و زمان 90 دقیقه از بیشینه سختی کمتری نسبت به دیگر نمونه‌ها برخوردار است، لذا می‌توان نتیجه گرفت که از لحاظ ترکیبات بین‌فلزی از شرایط بهتری نسبت به سایر نمونه‌ها برخوردار است. بیشترین مقدار استحکام برشی در دمای 1050 درجه سانتی‌گراد و زمان 90 دقیقه به میزان 270 مگاپاسگال بدست آمد.},
keywords_fa = {جوشکاری نفوذی, فولاد زنگ نزن مارتنزیتی 418, سوپرآلیاژ اینکونل 738, ریز ساختار, استحکام برشی.},

doi = { 10.47176/JWSTI.2024.17},
url = {http://jwsti.iut.ac.ir/article-1-459-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-459-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {Zeidabadinejad, H. and Rafiei, M. and Ebrahimzadeh, I. and Omidi, M. and Naeimi, F.},  
title = {The effect of bonding time on the microstructure and mechanical properties of WC-Co/Cu/St52   dissimilar joints by TLP}, 
abstract ={In this research, the transient liquid phase bonding of St52 carbon steel to WC-Co cermet using a copper interlayer with 50 μm thickness was done. For this purpose, samples were jointed to each other at a constant temperature of 1100 ºC and bonding times of 1, 15, 30, and 45 min. The microstructure of the joints was examined using an optical microscope and scanning electron microscope equipped with energy-dispersive X-ray spectroscopy. XRD analysis was also used to investigate the effect of bonding on the phase changes of the bonding area. Microhardness and tensile shear tests were also conducted to study the mechanical properties of the samples. Microstructural investigations showed the formation of three different zones including isothermal and athermal solidification zones and DAZ in the WC-Co base material side, which determine the characteristics of the samples. The isothermal solidification zone contained a Fe-rich solid solution and the athermal solidification zone contained a Cu-rich solid solution. η phase was not formed in the DAZ of WC-Co cermet at bonding times of 1 and 15 min. This phase was formed in the DAZ of WC-Co cermet by increasing the bonding time to 30 and 45 min. The microhardness studies showed that all samples had the same trend. Maximum microhardness was 1100 HV which was related to WC-Co base cermet and the lowest microhardness was about 220 HV which was related to steel base metal. Also, the maximum tensile-shear strength of the bonded samples was about 180 MPa for a bonded sample at a bonding time of 15 min, which was due to the increase in the volume fraction of iron-rich solid solution, as well as proper microstructural continuity and the presence of an optimal amount of copper-rich phase in the microstructure.},  
Keywords = {Transient liquid phase, St52, WC-Co, Microstructure, Shear tensile strength.},
volume = {10},
Number = {1}, 
pages = {65-81}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {تاثیر زمان اتصال بر ریزساختار و خواص مکانیکی اتصال غیرمشابه WC-Co/Cu/St52 با روش اتصال‌دهی فاز مایع گذرا},
abstract_fa ={در این پژوهش اتصال فاز مایع گذرای فولاد ساده کربنیSt52 به سرمت کاربید تنگستن- کبالت با استفاده از لایه میانی مس با ضخامت 50 میکرومتر مورد بررسی قرار گرفت. برای این منظور نمونه‌هایی در دمای 1100 درجه سانتی‌گراد و زمان‌های نگهداری 1، 15، 30 و 45 دقیقه به یکدیگر متصل شدند. ریزساختار اتصالات ایجاد شده با استفاده از میکروسکوپ نوری و میکروسکوپ الکترونی روبشی مجهز به سیستم آنالیز تفکیک انرژی بررسی شد. همچنین برای بررسی اثر اتصال بر تغییرات فازی ناحیه اتصال از آنالیز پراش پرتو ایکس استفاده شد. آزمایش‌های ریزسختی سنجی و تنش کششی برشی نیز جهت مطالعه خواص مکانیکی روی نمونه‌ها انجام شدند. بررسی‌های ریزساختاری نشان داد. سه منطقه مختلف انجمادی هم‌دما و غیرهم‌دما و منطقه متأثر از نفوذ سمت ماده پایه WC-Co  وجود دارد که ویژگی‌ نمونه‌ها را تعیین می‌کنند. منطقه انجماد همدما حاوی محلول جامد غنی از آهن و منطقه انجماد غیرهمدما حاوی فاز محلول جامد غنی از مس بود. در منطقه متأثر از نفوذ سمت سرمت WC-Co در زمان‌های 1 و 15 دقیقه فاز η ایجاد نگردید در حالی‌که با افزایش زمان اتصال به 30 و نهایتا 45 دقیقه فاز η در منطقه متأثر از نفوذ سمت سرمت WC-Co تشکیل شد. پروفیل ریز سختی برای تمامی نمونه‌ها دارای یک روند بود و حداکثر سختی مربوط به سرمت پایه WC-Co به میزان 1100 ویکرز و کمترین سختی مربوط به فلزپایه فولادی و حدود 220 ویکرز بود. همچنین حداکثر استحکام کششی برشی مربوط به نمونه متصل شده در زمان 15 دقیقه و حدود 180 مگاپاسکال بود که به دلیل افزایش در کسر حجمی محلول جامد غنی از آهن و همچنین پیوستگی ریزساختاری مناسب و وجود مقدار بهینه  فاز غنی از مس در ریزساختار بدست آمد.},
keywords_fa = {اتصال فاز مایع گذرا, فولاد St52, سرمت WC-Co, ریزساختار, خواص مکانیکی.},

doi = { 10.47176/JWSTI.2024.18},
url = {http://jwsti.iut.ac.ir/article-1-463-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-463-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {Abbasi, R. and AkbariMousavi, S. A.A. and Vahidshad, Y.},  
title = {Optimization weldability of Haynes 25 cobalt base superalloy with pulsed fiber laser}, 
abstract ={The present study focuses on optimizing the mechanical properties and microstructure of laser welding in Haynes 25 (L-605) cobalt-based superalloy. Initially, the influence of laser welding variables such as laser power, pulse frequency, welding speed, and pulse width on the mechanical and metallurgical properties of the weld joints is investigated. By examining the welding variables, the values of G (thermal gradient) and R (cooling rate) are calculated, and their ratio (G/R) and cooling rate (G×R), which predominantly affect the solidification microstructure, are determined. The structural correlation with the mechanical properties resulting from welding is examined.  In this research, it is considered to obtain the welding variables to create a high percentage of the structure in the form of equiaxed dendrite. Microstructural analysis reveals the growth of equiaxed grains and dendritic structures in the weld zone. The high cooling rate in the weld pool leads to dendritic solidification starting from columnar dendrites at the weld walls and ending in equiaxed dendrites at the center of the weld. The microhardness value in the weld zone is HV 328, which is very close to the microhardness of the base material. The tensile strength of the weld samples reaches about 93% to 94% of the base metal tensile strength. Tensile testing of the weld samples indicates a ductile-brittle fracture. Examination of the scanning electron microscope confirms the presence of dimples, intergranular cracks, and microvoids in the fracture zone.  },  
Keywords = {Haynes 25, microstructure, mechanical properties, fiber laser welding, dendritic growth, fractography.},
volume = {10},
Number = {1}, 
pages = {83-97}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {بهینه‌سازی جوش‌پذیری ابرآلیاژ پایه کبالت هاینس 25 با لیزر فیبری ضربانی},
abstract_fa ={مطالعه حاضر بهینه‌سازی خواص مکانیکی و ریزساختاری جوشکاری لیزر ابر آلیاژ پایه کبالت هاینس 25 (L-605) را بررسی می‌کند. تأثیر متغیرهای جوشکاری لیزر مانند قدرت پرتو لیزر، بسامد ضربانی، سرعت جوشکاری و پهنای زمانی ضربان بر خواص مکانیکی و متالورژیکی اتصالات جوش مورد بررسی قرار می‌گیرد. با بررسی متغیرهای جوشکاری مقادیر G (شیب حرارتی) و R (نرخ انجماد) و  همچنین تحت تبرید (G/R) و سرعت سرمایش (G×R) که بر ریزساختار انجماد غالب هستند، محاسبه و همبستگی ساختاری با خواص مکانیکی حاصل از جوش بررسی می‌گردد. در این تحقیق بدست آوردن متغیرهای جوشکاری برای ایجاد درصد بالایی از ساختار به صورت دندریت هم محور‌مد نظر می‌باشد. بررسی ریزساختاری رشد دانه همپایی و ساختارهای دندریتی در ناحیه جوش را نشان می‌دهد. سرعت انجماد بالا در حوضچه جوش سبب انجماد دندریتی شد که از دندریت‌های ستونی دیواره‌های جوش شروع می‌شود و به دندریت‌های هم محور در مرکز جوش منتهی می‌شود. مقدار ریزسختی در ناحیه جوش برابر 328 ویکرز می‌باشد که به سختی ماده اصلی بسیار نزدیک است. استحکام کششی نمونه‌های جوش به حدود %93 و%94 استحکام کشش فلزپایه می‌رسد. بررسی آزمون کشش نمونه‌های جوش حاکی از شکست نرم-ترد است. با بررسی میکروسکوپی الکترونی روبشی وجود فرورفتگی‌ها، شکاف بین دانه‌ای و ریز حفره‌ها در ناحیه شکست تأیید شد.},
keywords_fa = {هاینس 25, ریزساختار, خواص مکانیکی, جوش لیزر فیبر, رشد همپایی, شکست نگاری},

doi = { 10.47176/JWSTI.2024.19},
url = {http://jwsti.iut.ac.ir/article-1-460-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-460-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {Nourmohammadi, M. H. and Movahedi, M. and Kokabi, A. H.},  
title = {Investigating the electromigration resistance of composite lead-free solder alloy containing cobalt particles}, 
abstract ={In today's technological landscape, the push for miniaturization in electronic devices is greater than ever, driven by technological advancements.The challenges of electromigration and thermomigration have arisen due to the need to establish new electronic connections under conditions characterized by creeping temperatures, originating from the low melting point of solders and high current density.  Therefore, recently, alloying and composite materials have been employed to enhance the resistance of electronic connections to electromigration. In this study, efforts to enhance the resistance to electromigration using a composite SAC0307 lead-free solder alloy incorporating cobalt microparticles. The presence of cobalt in the intermetallic composition of the interface causes more stability of the intermetallic composition of the interface and prevents the reduction of the thickness of the intermetallic composition of the interface during the time of the electromigration test; As a result, the stability and electronic connection of the sample soldered with composite solder alloy is more than that of non-composite solder alloy. On the other hand, due to the fine grain structure and the increase in grain boundary density in the composite solder alloy, the lattice diffusion mechanism in the non-composite solder alloy has been changed to the grain boundary diffusion mechanism; As a result, due to the consumption of copper atoms flowed from the cathode side to the anode by the intermetallic compounds present in the grain boundaries, non-uniform microstructural was observed in the composite solder alloy during the time of electromigration test.},  
Keywords = {Lead-free solders, electromigration, Soldering, Intermetallic compound, Accumulative Roll Bonding.},
volume = {10},
Number = {1}, 
pages = {99-108}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {بررسی مقاومت به مهاجرت الکترونی آلیاژ لحیم بدون سرب کامپوزیتی حاوی ذرات کبالت},
abstract_fa ={امروزه با پیشرفت روز افزون تکنولوژی، تقاضا برای کوچک‌سازی وسایل الکترونیکی بیشتر از پیش مورد نیاز است. قرارگیری اتصالات الکترونیکی جدید در شرایط دمایی خزشی به دلیل نقطه ذوب پایین لحیم‌ها و همین‌طور دانسیته جریان بالا چالش‌هایی مانند مهاجرت الکترونی و حرارتی به وجود آورده است. لذا اخیراً آلیاژسازی و کامپوزیت‌سازی جهت بهبود مقاومت به مهاجرت الکترونی اتصالات الکترونیکی به کار گرفته شده است. در این پژوهش سعی بر آن شد با کامپوزیت سازی آلیاژ لحیم بدون سرب SAC0307 با استفاده از میکروذرات کبالت، مقاومت به مهاجرت الکترونی بهبود یابد. حضور کبالت در ترکیب بین فلزی فصل مشترکی باعث پایداری بیشتر ترکیب بین فلزی فصل مشترکی و جلوگیری از کاهش ضخامت ترکیب بین فلزی فصل مشترکی در طی زمان آزمون مهاجرت الکترونی می‌شود؛ درنتیجه پایداری و برقراری اتصال الکترونیکی نمونه لحیم‌کاری شده با آلیاژ لحیم کامپوزیتی بیشتر از آلیاژ لحیم غیرکامپوزیتی است. از طرفی دیگر، به دلیل ساختار ریزدانه و افزایش چگالی مرزدانه‌ها در آلیاژ لحیم کامپوزیتی، مکانیزم نفوذ شبکه ای در آلیاژ لحیم غیرکامپوزیتی به مکانیزم نفوذ مرزدانه تغییر یافته است؛ در نتیجه به دلیل مصرف اتم‌های مس شارش یافته از سمت کاتد به آند توسط ترکیبات بین فلزی موجود در مرزدانه‌ها، در آلیاژ لحیم کامپوزیتی طی زمان آزمون مهاجرت الکترونی غیریکنواختی ریزساختاری مشاهده شد.},
keywords_fa = {لحیم‌های نرم بدون سرب؛ مهاجرت الکترونی؛ لحیم کاری؛ کامپوزیت‌های زمینه فلزی؛ ترکیبات بین فلزی؛ اتصال نورد انباشتی.},

doi = { 10.47176/JWSTI.2024.20},
url = {http://jwsti.iut.ac.ir/article-1-462-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-462-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {Maraki, M. R. and Tagimalek, H. and Yousefieh, M. and Aghaeifar, A. and Foorginejad, A.},  
title = {Feasibility and determination of the characteristics of the replacement of arc and wire additive manufacturing process based on gas metal arc welding for the construction of bridges and metal structures: Approach of artificial intelligence algorithms}, 
abstract ={Society's great and growing demand for buildings and structures has created the need to apply new construction methods to shorten construction times, make buildings lighter, extend their useful life, and make them more earthquake-proof. In the long term, the new methods will lead to structural optimization, increased building performance, and the achievement of optimal operating conditions. New technologies are meeting society's increasing need for special structures more than ever. Additive manufacturing is based on gas metal arc welding as one of the fastest and most cost-effective manufacturing methods for primary metal structures. For this purpose, the three parameters voltage, wire feed speed, and welding speed were considered initial parameters affecting the width and height of the welding flux. To investigate the effects of the process, 16 experiments with input parameters were evaluated. The width and height of the sweat pollen were determined by experimental investigations. Subsequently, the resulting welding geometry is modeled using three numerical modeling methods, including intensive learning machines, relevence vector machine, and fuzzy logic. The comparison between the experimental data and the results of the three generated models shows that fuzzy logic comes closest to the experimental data of the welding geometry of the modeling methods. For example, the test data of the generative fuzzy model resulted in an average error for height and width of 0.667 and 0.5477, respectively, and a root mean square error for height and width of 0.0046 and 0.3, respectively, which expresses the generalization ability and reliability compared to other modeling methods in this process. Finally, a metal pattern of a special structure was produced based on arc and wire additive manufacturing based gas metal arc welding.  },  
Keywords = {Arc and wire additive manufacturing, metal structures, artificial intelligence algorithms, gas metal arc welding.},
volume = {10},
Number = {1}, 
pages = {109-120}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {امکان‌سنجی و مشخصه‌یابی جایگزینی روش ساخت افزایشی قوس و سیم مبتنی بر جوشکاری قوس الکتریکی با گاز محافظ برای ساخت پل و سازه‌های فلزی: رویکرد الگوریتم‌های هوش مصنوعی},
abstract_fa ={نیاز گسترده و روزافزون جامعه به ساختمان و سازه، ضرورت استفاده از روش‌های ساخت جدید به منظور افزایش سرعت ساخت، سبک‌سازی، افزایش عمر مفید و نیز مقاوم نمودن ساختمان‌ها در برابر زلزله را بیش از پیش مطرح ساخته است. روش‌های جدید، در دراز مدت موجب بهینه‌سازی سازه، افزایش ساخت و رسیدن به شرایط اجرایی مطلوب خواهد شد. نیاز روز افزون جوامع بشری به سازه‌های خاص توسط فناوری جدید بیشتر از پیش احساس می‌شود. ساخت افزایشی برپایه جوشکاری قوس الکتریکی با گاز محافظ به عنوان یکی از روش‌های ساخت سریع و کم‌هزینه برای سازه‌های اولیه فلزی است. بدین منظور سه پارامتر ولتاژ، سرعت تغذیه سیم و سرعت جوشکاری به ‌عنوان پارامترهای تأثیرگذار بر عرض و ارتفاع گرده جوش به عنوان پارامترهای خروجی در نظر گرفته شده‌اند. برای بررسی اثرات فرایند، 16 آزمایش با پارامتر ورودی مورد ارزیابی قرار گرفت. با انجام آزمایش‌های تجربی نتایج عرض و ارتفاع گرده جوش تعیین شد. سپس هندسه جوش حاصله به سه روش مدل‌سازی عددی که شامل ماشین یادگیری شدید، ماشین بردار ارتباط و منطق فازی مدل‌سازی شده است. مقایسه بین داده‌های تجربی و خروجی سه مدل ایجادی نشان می‌دهد که نزدیک‌ترین نتایج به داده‌های تجربی هندسه جوش از روش‌های مدل‌سازی، منطق فازی دارا بوده است. به گونه‌ای که داده‌های آزمون مدل فازی ایجادی، خطای میانگین برای ارتفاع و عرض به ترتیب 667/0 و 5477/0 و جذر میانگین مربعات برای ارتفاع و عرض 0046/0 و 3/0 بدست آورده که بیان‌کننده قابلیت تعمیم و اطمینان بالا نسبت به دیگر روش مدل‌سازی در این فرایند است. در نهایت نمونه فلزی سازه خاص مبتنی برساخت افزایشی قوس و سیم برپایه جوشکاری قوس الکتریکی با گاز محافظ تولید شد.},
keywords_fa = {ساخت افزایشی قوس و سیم, سازه‌های فلزی, الگوریتم‌های هوش مصنوعی, جوشکاری قوس الکتریکی با گاز محافظ.},

doi = { 10.47176/JWSTI.2024.21},
url = {http://jwsti.iut.ac.ir/article-1-442-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-442-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {Taheri, M. and Azimiroeen, Gh. and Shamanian, M. and Bahrami, A.},  
title = {Evaluation of dissimilar bonding of Alumina to copper with Active Filler Metal Ag-Cu-Ti-Sn and Ag-Cu-Ti-Sn-%3.5Zr by Induction Brazing method}, 
abstract ={The dissimilar joint of alumina to copper with active filler metals Ag-Cu-Ti-Sn and Ag-Cu-Ti-Sn-%3.5Zr were done using the induction brazing process at temperatures of 840 and 860 ℃ for 15 minutes. The microstructures of joints were evaluated using optical microscope (OM) and scanning electron microscope (SEM). Vickers hardness test and shear tensile strength test were used to evaluate the mechanical properties. The results of the microstructural studies showed that the Al2O3/Cu joints using Ag-Cu-Ti-Sn and Ag-Cu-Ti-Sn-%3.5Zr fillers contain a reaction layer at the interface between alumina and the filler metal. At the area of the reaction layer with Ag-Cu-Ti-Sn filler metal, two TiO and Cu3Ti3O phases were observed, and also at the reaction layer with Ag-Cu-Ti-Sn-%3.5Zr filler metal, two TiO and ZrO2 phases were observed. The results of the shear strength test showed that due to the greater thickness of the filler metal and the lower thickness of the reaction layer, the joint with the filler metal Ag-Cu-Ti-Sn-%3.5Zr (14 MPa) has a higher shear strength as compared with the joint with filler metal Ag-Cu-Ti- Sn (9 MPa).},  
Keywords = {Induction Brazing, Active filler metal, Dissimilar joint, Alumina, Microstructure.},
volume = {10},
Number = {1}, 
pages = {121-132}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {ارزیابی اتصال غیرهمجنس آلومینا به مس با فلز پرکننده فعال  Ag-Cu-Ti-Sn و Ag-Cu-Ti-Sn-%3.5Zr به روش لحیم کاری سخت القایی},
abstract_fa ={اتصال غیرهمجنس آلومینا به مس با فلزات پرکننده فعال Ag-Cu-Ti-Sn و Ag-Cu-Ti-Sn-%3.5Zr با استفاده از فرایند لحیم-کاری سخت القایی بترتیب در دماهای 840 و 860 درجه سانتی گراد به مدت 15 دقیقه انجام شدند. ریزساختار اتصالات با استفاده از میکروسکوپ نوری (OM) و میکروسکوپ الکترونی روبشی (SEM) مورد مطالعه قرار گرفت. برای ارزیابی خواص مکانیکی از آزمون ریزسختی ویکرز و آزمون استحکام کشش برشی استفاده شد. بررسی های ریزساختاری نشان داد که اتصال Al2O3/Cu با استفاده از پرکننده های Ag-Cu-Ti-Sn و Ag-Cu-Ti-Sn-%3.5Zr منجر به تشکیل یک لایه واکنشی در فصل مشترک آلومینا و فلز پرکننده می شود. در لایه‌ی واکنشی اتصال با فلز پرکننده Ag-Cu-Ti-Sn، دو فاز TiO و Cu3Ti3O و در اتصال با فلز پرکننده Ag-Cu-Ti-Sn-%3.5Zr دو فاز TiO و ZrO2 مشاهده شد. نتایج آزمون استحکام برشی نشان داد که به دلیل ضخامت بیشتر فلز پرکننده و ضخامت کمتر لایه واکنشی، اتصال با فلز پرکننده Ag-Cu-Ti-Sn-%3.5Zr استحکام برشی (14MPa) بالاتری نسبت به اتصال با فلز پرکننده Ag-Cu-Ti-Sn (9MPa) دارد.},
keywords_fa = {لحیم‌کاری سخت القایی, فلز پرکننده فعال, اتصال غیرهمجنس, آلومینا, ریزساختار},

doi = { 10.47176/JWSTI.2024.22},
url = {http://jwsti.iut.ac.ir/article-1-468-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-468-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {Khalaj, Gh. and Khalaj, J. and Soleymani, F.},  
title = {Investigation of the Joint Interface in Explosive Welding of Austenitic Stainless Steel 321 - Aluminum 1050 - Aluminum 5083 after Heat Treatment}, 
abstract ={In this study, the microstructure of the joint interface in three-layer explosive welding of austenitic stainless steel 321 - aluminum 1050 - aluminum 5083 was examined before and after heat treatment. The welded samples were subjected to heat treatment at temperatures of 250°C and 350°C for durations of 1000, 3000, and 10000 seconds. Microstructural analysis was performed using optical microscopy and scanning electron microscopy. The results revealed that under all conditions, the Joint Interface of aluminum 5083 - aluminum 1050 exhibited a flat and defect-free structure. With increasing standoff distance, the Joint Interface of stainless steel 321 - aluminum 1050 transitioned from a smooth to a wavy pattern, and the average layer thickness increased from 4.95 μm to 6.7 μm. During heat treatment, the layer thickness in the Joint Interface increased proportionally to the diffusion kinetics, reaching maximum values of 18.56 μm and 15.02 μm for samples with standoff distances of 6.75 mm and 6 mm, respectively. The activation energies for diffusion were calculated as 46.6 kJ/mol and 42.4 kJ/mol, and the diffusion constants were 142.2 ms-1  and 45.3 ms-1 for the same samples.  },  
Keywords = {Heat treatment, explosive welding, Joint Interface, standoff distance, reaction layer, diffusion.},
volume = {10},
Number = {1}, 
pages = {133-143}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {بررسی فصل مشترک اتصال انفجاری فولاد  زنگ‌نزن آستنیتی 321 - آلومینیوم 1050 - آلومینیوم 5083 پس از عملیات حرارتی},
abstract_fa ={در این پژوهش ریزساختار فصل‌مشترک اتصال جوشکاری انفجاری سه لایه فولاد زنگ‌نزن آستنیتی 321- آلومینیوم 1050 - آلومینیوم 5083 با دو فاصله توقف 6 و 75/6 میلی‌متر، قبل و بعد از عملیات‌حرارتی بررسی شد. عملیات‌حرارتی نمونه‌های جوشکاری شده در دماهای C◦250و 350 برای زمان‌های1000، 3000 و 10000 ثانیه، انجام شد. بررسی ریزساختار با استفاده از میکروسکوپ نوری و میکروسکوپ الکترونی روبشی انجام شد. نتایج نشان داد که در همه شرایط فصل‌مشترک آلومینیوم 5083- آلومینیوم 1050 به صورت مسطح و با ساختار بدون نقص است. با افزایش فاصله توقف، فصل‌مشترک فولاد زنگ‌نزن آستنیتی 321- آلومینیوم 1050 از حالت صاف به حالت موجی تبدیل شده و همچنین متوسط ضخامت لایه فصل‌مشترک از 95/4 به 7/6 میکرون افزایش می‌یابد. در حین عملیات حرارتی، ضخامت لایه فصل‌مشترک متناسب با سینتیک نفوذ افزایش می‌یابد و در بیشترین مقدار به 56/18 و 02/15 میکرون به‌ترتیب برای نمونه با فاصله توقف 75/6 و 6 میلی‌متر می‌رسد. برای نمونه با فاصله توقف 75/6 و 6 میلی‌متر مقادیر انرژی محرکه نفوذ به‌ترتیب 6/46 وkJ/mol 4/42 و مقادیر ثابت نفوذ به ترتیب 2/142و ms-1 3/45 محاسبه شد.},
keywords_fa = {عملیات حرارتی, جوشکاری انفجاری, فصل مشترک, فاصله توقف, لایه واکنشی, نفوذ},

doi = { 10.47176/JWSTI.2024.23},
url = {http://jwsti.iut.ac.ir/article-1-470-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-470-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {Nourmohammadi, M. H. and Movahedi, M. and Kokabi, A. H.},  
title = {Development of lead-free soft solder alloy via accumulative roll bonding}, 
abstract ={Soldering plays a crucial role in the electronics industry, driving the need for constant improvements in physical and mechanical properties and the management of intermetallic compound formation. Research in composite materials aims to achieve a uniform distribution of reinforcing particles within solder matrix to enhance their performance. This study investigates the integration of cobalt microparticles into SAC0307 lead-free soft solder alloy using the accumulative roll bonding (ARB) method. Microstructural analysis confirmed a homogeneous dispersion of cobalt particles within the solder after three ARB passes. Moreover, increasing cobalt content led to a reduction in the size of Cu6Sn5 intermetallic compounds, from 9 µm to 5 µm with 1% cobalt by weight. Examination of β-Sn grain morphology revealed the impact of cobalt particles on recovery and recrystallization kinetics in the solder. Mechanical testing indicated a 20% decrease in interlayer strength within composite solder sheets. Tensile tests showed a 28% increase in strength and a 31% decrease in elongation for composite solder alloy containing 1% cobalt. Differential scanning calorimetry (DSC) results revealed minimal change in the melting temperature of composite solder foil.  },  
Keywords = {Lead-free solders, Metal composites, Intermetallic compound, Microstructure, Accumulative Roll Bonding.},
volume = {10},
Number = {2}, 
pages = {1-12}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {کامپوزیت‌سازی آلیاژلحیم نرم بدون سرب به روش اتصال نورد انباشتی},
abstract_fa ={لحیم‌کاری نرم از پرمصرف‌ترین فرایندهای اتصال‌دهی در صنعت الکترونیک است. بهبود خواص فیزیکی و مکانیکی و همچنین کنترل تشکیل و رشد ترکیبات بین‌فلزی، زمینه‌ساز گسترش تحقیقات در زمینه کامپوزیت‌سازی شده است. توزیع یکنواخت از ذرات سخت در زمینه لحیم، ‌طوری‌که خواص فیزیکی و مکانیکی را بهبود بخشد می‌تواند معیاری موفقیت‌آمیز برای رسیدن به آلیاژهای لحیم کامپوزیتی باشد. در این پژوهش با بهره‌گیری از روش اتصال‌دهی نورد انباشتی (ARB)، کامپوزیت‌سازی آلیاژ لحیم نرم بدون سرب SAC0307 با استفاده از میکروذرات کبالت انجام شد. در ادامه جهت بررسی کارایی روش کامپوزیتی به کارگرفته شده، ورق‌های لحیم تولید شده به این روش از نظر ریزساختاری، مکانیکی و فیزیکی مورد بررسی قرار گرفت. بررسی‌های ریزساختاری نشان‌دهنده توزیع مناسب ذرات تقویت کننده کبالت درزمینه لحیم بعد از3 پاس ARB بود. همچنین، با افزایش درصد کبالت اندازه ترکیبات بین فلزی Cu6Sn5 در آلیاژ لحیم غیرکامپوزیتی ازµmم9 به µmم5 در آلیاژ لحیم کامپوزیتی با 1 درصد وزنی کبالت کاهش یافت. در ادامه با بررسی تغییرات شکل و اندازه دانه های β-Sn، وقوع و تسریع فرایند‌های ترمیمی (بازیابی و تبلور مجدد) با حضور ذرات تقویت کننده کبالت در زمینه لحیم نشان داده شد. بررسی‌های خواص مکانیکی ورق‌های تولید شده، افت 20 درصدی استحکام مکانیکی اتصال بین لایه‌های ورق لحیم کامپوزتی را نشان داد. همچنین، نتایج آزمون کشش نشان‌دهنده افزایش 28 درصدی استحکام کششی و کاهش 31 درصدی ازدیاد طول آلیاژ لحیم کامپوزیتی با 1 درصد وزنی کبالت است. از طرفی نتایج آزمونDSC، تغییر ناچیز دمای ذوب ورق‌های آلیاژ لحیم کامپوزیتی را نشان داد.},
keywords_fa = {لحیم های نرم بدون سرب؛ کامپوزیت های زمینه فلزی؛ ترکیبات بین فلزی؛ ریزساختار؛ اتصال نورد انباشتی},

doi = {10.47176/JWSTI.2025.01 },
url = {http://jwsti.iut.ac.ir/article-1-461-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-461-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {B.Heidari-Dehkordi, B. and Rafiei, M. and Omidi, M. and Abbasi-Baharanchi, M.},  
title = {The effect of operation time and interlayer thickness on properties of AISI316L/BNi-2/WC-Co bonding system by TLP}, 
abstract ={In this study, 316L stainless steel and WC-10Co cermet were bonded by transient liquid phase process with BNi-2 interlayers with different thicknesses of 25 and 50 μm. The bonding process was conducted at 1050 °C for 1, 15, and 30 min. After bonding, the microstructure of the joints was examined using optical microscopy and scanning electron microscopy equipped with energy-dispersive X-ray spectroscopy. Microhardness and tensile-shear tests were also performed to study the mechanical properties of the bonded samples. Microstructural analyses revealed that the formation mechanism of the solidified region in all samples was isothermal solidification, resulting in an isothermal solidification zone upon bonding. Additionally, the only phase present in the isothermal solidification zone was a nickel-based solid solution. In the diffusion-affected zone of the steel base material, complex borides formed regardless of the interlayer thickness. In the diffusion-affected zone of the WC-Co material, a brittle eta phase formed. Microhardness tests indicated that the maximum hardness in all samples was approximately 1100 Vickers, which was attributed to the presence of hard WC particles in the WC-Co base material. Furthermore, the highest tensile-shear strength, approximately 240 MPa, was observed in the bonded sample for 15 min with 50 μm thickness interlayer.},  
Keywords = {Transient liquid phase bonding, 316L steel, WC-Co, microstructure, Mechanical behavior},
volume = {10},
Number = {2}, 
pages = {13-30}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {تأثیر زمان عملیات و ضخامت لایه واسطه بر خواص سیستم اتصالی  AISI316L/BNi-2/WC-Co با روش فاز مایع گذرا},
abstract_fa ={در این پژوهش فولاد زنگ‌نزن 316L و سرمت WC-10Co توسط روش اتصال فاز مایع گذرا با استفاده از لایه میانی BNi-2 در دو ضخامت 25 و 50 میکرومتر به یکدیگر متصل شدند. فرایند اتصال نمونه‌ها در دمای 1050 درجه سانتی‌گراد و در زمان‌های نگهداری 1، 15 و 30 دقیقه انجام شد. پس از انجام عملیات اتصال ریزساختار اتصالات ایجاد شده با استفاده از میکروسکوپ نوری و میکروسکوپ الکترونی روبشی مجهز به سیستم آنالیز تفکیک انرژی مورد بررسی قرار گرفت. آزمایش‌های ریزسختی سنجی و تنش کششی-برشی نیز جهت مطالعه رفتار مکانیکی نمونه‌ها انجام گرفت. بررسی‌های ریزساختاری نشان داد که مکانیزم شکل‌گیری ناحیه انجمادی در تمامی نمونه‌ها، مکانیزم انجماد همدما بوده و در اثر انجام اتصال یک ناحیه انجمادی همدما ایجاد می‌شود. همچنین تنها فاز موجود در منطقه انجمادی هم دما محلول جامد پایه نیکلی بود. در منطقه متأثر از نفوذ سمت ماده پایه فولادی فارغ از ضخامت لایه میانی بورایدهای کمپلکس و در منطقه متأثر از نفوذ سمت ماده WC-Co فاز ترد و شکننده اتا ایجاد شد. بررسی ریزسختی نمونه‌ها نشان داد که حداکثر سختی در تمامی نمونه‌ها متعلق به ماده پایه WC-Co و در حدود 1100 ویکرز بوده که دلیل آن وجود ذرات سخت WC بود. همچنین حداکثر استحکام کششی-برشی حدود 240 مگاپاسکال و متعلق به نمونه متصل شده در زمان 15 دقیقه با استفاده از لایه میانی با ضخامت 50 میکرومتر بود.},
keywords_fa = {اتصال فاز مایع گذرا, فولاد L 316, WC-Co, ریزساختار, رفتار مکانیکی},

doi = {10.47176/JWSTI.2025.02},
url = {http://jwsti.iut.ac.ir/article-1-466-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-466-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {Heidarzadeh, A. and Khajeh, R. and Sajed, M.},  
title = {The effect of nickel powder and tool penetration depth on microstructure and mechanical properties of friction stir lap welded aluminum-copper joints}, 
abstract ={In this research, the effect of nickel powder as an interlayer and the tool penetration depth on the microstructure and mechanical properties of lap joints between aluminum 1050 (top sheet) and pure copper (bottom sheet), both with a thickness of 2 mm, was investigated. Nickel powder was added through a machined groove with a width and depth of 1 mm at the base of the aluminum sheet. Friction stir lap welding was performed using a hot work steel tool with a shoulder diameter of 16 mm, a pin diameter of 4 mm, a pin height of 2.1 mm, a rotational speed of 950 rpm, a feed rate of 85 mm/min, a tool tilt angle of 2°, and varying tool penetration depths of 0, 0.05, and 0.1 mm. The results revealed that in the sample with a 0 mm penetration depth, due to insufficient heat generation, defects such as tunnel voids were formed. Increasing the penetration depth to 0.05 mm resulted in the formation of uniform and thin intermetallic layers, including Al3Ni2, Al7Cu4Ni, and Cu3.8Ni at the interface, which enhanced joint quality and increased tensile strength to 185.2 MPa with a fracture strain of 8.7%. In the sample with a 0.1 mm penetration depth, thicker and less uniform intermetallic layers were formed, which, despite locally increasing hardness, led to a decrease in tensile strength and fracture strain to 136.6 MPa and 6.7%, respectively. This study demonstrates that under the conditions of this research, a tool penetration depth of 0.05 mm provides the optimal conditions for FSLW of aluminum-copper alloys using nickel powder.},  
Keywords = {Friction stir welding, Copper, Aluminum, Nickel powder.},
volume = {10},
Number = {2}, 
pages = {31-39}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {تاثیر پودر نیکل و عمق نفوذ ابزار بر ریزساختار و خواص مکانیکی جوش همزن اصطکاکی لب‌ روی‌هم آلومینیم-مس},
abstract_fa ={در این پژوهش، تأثیر پودر نیکل به عنوان لایه واسط و عمق نفوذ ابزار بر ریزساختار و خواص مکانیکی اتصالات لب‌روی‌هم ورق آلومینیم 1050 (ورق فوقانی) و مس خالص (ورق تحتانی) هر دو به ضخامت 2 میلیمتر بررسی شده است. جهت اضافه نمودن پودر نیکل از یک شیار تراشیده شده به عرض و عمق 1 میلیمتر در کف ورق آلومینیم استفاده گردید. جوشکاری همزن اصطکاکی لب‌روی‌هم با استفاده از ابزار فولاد گرم‌کار با قطر شانه، قطر و ارتفاع پین به ترتیب برابر با 16، 4 و 1/2 میلیمتر، سرعت چرخش ابزار 950 دور بر دقیقه، سرعت پیشروی ابزار 85 میلیمتر بر دقیقه، زاویه ابزار 2 درجه و عمق نفوذ ابزار متفاوت برابر با صفر، 05/0 و 1/0 میلیمتر انجام شد. نتایج نشان داد که در نمونه‌ای با عمق نفوذ صفر، به دلیل عدم تولید حرارت کافی و تغییرشکل پلاستیک مناسب و متعاقب آن ایجاد عیوبی مانند نقص‌های تونلی اتفاق افتاد. با افزایش عمق نفوذ ابزار به 05/0 میلیمتر، ترکیبات بین‌فلزی Al3Ni2، Al7Cu4Ni و Cu3.8Ni به صورت یکنواخت و نازک در ناحیه فصل مشترک تشکیل شده و منجر به بهبود کیفیت اتصال و افزایش استحکام کششی تا 2/185 مگاپاسکال و کرنش شکست 7/8 درصد شد. در نمونه‌ای با عمق نفوذ 1/0 میلیمتر، ترکیبات بین‌فلزی ضخیم‌تر تشکیل شدند که با وجود افزایش سختی موضعی، منجر به کاهش استحکام کششی و کرنش شکست به ترتیب به 6/136 مگاپاسکال و 7/6 درصد گردید. این مطالعه نشان می‌دهد که در شرایط تهیه نمونه‌های جوشکاری در تحقیق حاضر، عمق نفوذ 05/0 میلیمتر بهینه‌ترین شرایط را برای جوشکاری همزن اصطکاکی لب روی هم آلومینیم-مس در حضور پودر نیکل فراهم می‌کند.},
keywords_fa = {جوشکاری همزن اصطکاکی, مس, آلومینیم, پودر نیکل.},

doi = {10.47176/JWSTI.2025.03},
url = {http://jwsti.iut.ac.ir/article-1-473-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-473-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {AbediChermahini, H. and Piran, M. and EsmaeiliChamgordani, A. and Atapoor, M.},  
title = {Investigating the mechanical behavior and microstructure of AISI 316L stainless steel sheets welded by resistance spot welding method using copper interface layer}, 
abstract ={In this research, the mechanical and microstructural properties of AISI 316L sheets welded by RSW method using copper interlayer were investigated. In this regard, two types of connections were made, one without the use of an interlayer and the other with the use of a copper interlayer in different currents. In order to choose the optimal current for both types of connections, tensile tests were first performed, and microstructural, microhardness, elemental evaluation and failure mode tests were conducted on the selected samples. According to the obtained results, by increasing the electric current, the heat input in the welding pool is sufficiently high and the microstructural and mechanical properties of the welding zone were improved(Conversion of coarse grain to fine grain). Also, due to the optimality of the electric current in both samples with and without the interface layer, both samples had environmental failure, which indicates the high strength of the interface and their welding point. Changes in the chemical composition in different welding zones were insignificant and the distribution of elements was uniform in all zones. Also, the hardness changes from the base metal to the center of the welding zone were in the order of welding zone > base metal > heat-affected zone, which was consistent with the results obtained from the microstructural investigations. According to the results obtained for both cases with and without the use of an interface layer, the resistance spot welding method showed a successful connection for both types of cases.},  
Keywords = {AISI 316L Sheet, Copper Interlayer, Resistance Spot Welding.},
volume = {10},
Number = {2}, 
pages = {41-50}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {بررسی رفتار مکانیکی و ریزساختار ورق‌های فولاد زنگ‌نزن  AISI316L  جوش‌داده‌شده به روش جوشکاری مقاومتی نقطه‌ای با استفاده از لایه واسط مس},
abstract_fa ={در پژوهش حاضر به بررسی خواص مکانیکی و ریزساختار ورق‌های فولاد زنگ نزن گرید L316 جوش داده شده به روش جوشکاری مقاومتی نقطه‌ای با استفاده از لایه واسط مس پرداخته شد. در همین راستا دو حالت، یکی بدون استفاده از لایه واسط و دیگری با استفاده از لایه واسط مس در جریان‌های مختلف اتصال داده شدند. به منظور انتخاب جریان بهینه برای هر دو نوع اتصال ابتدا آزمون کشش انجام شد. پس از آن بررسی‌های ریزساختاری، ارزیابی‌های ریزسختی، توزیع عنصری و حالت شکست بر روی نمونه‌های بهینه انجام شد. بنابر نتایج بدست آمده با افزایش جریان الکتریکی حرارت ورودی در حوضچه جوش تا حد مناسبی بالا رفته و خواص مکانیکی با ریزتر شدن دانه‌های ناحیه جوش بهبود یافته است. همچنین بدلیل بهینه بودن جریان الکتریکی در هر دو نمونه "با و بدون" لایه واسط، هر دو نمونه دچار شکست محیطی شدند که نشان از استحکام بالای فصل مشترک و نقطه جوش آن‌ها دارد. تغییرات ترکیب شیمیایی در نواحی مختلف جوش ناچیز بوده و توزیع عناصر در تمامی نواحی یکنواخت گزارش شد. همچنین بیشترین سختی با حرکت از سمت فلز پایه به سمت مرکز جوش به فلز جوش اختصاص داشت و سپس به ترتیب فلز پایه و ناحیه متاثر از حرارت قرار داشتند. با نتایج بدست آمده از بررسی‌های ریزساختاری نیز مطابقت داشت.},
keywords_fa = {جوشکاری همزن اصطکاکی, مس, آلومینیم, پودر نیکل.},

doi = {10.47176/JWSTI.2025.04},
url = {http://jwsti.iut.ac.ir/article-1-477-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-477-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {MizabiAsl, M. and Belbasi*, M.},  
title = {Evaluation of heat input on microstructural and mechanical properties of dissimilar joints of  D6AC steel to VCN 200 (1.6580) in GTAW welding}, 
abstract ={In this research, the effect of heat input on the microstructure and mechanical properties of the joint of two dissimilar steels D6AC and VCN 200 steel was investigated. For this purpose, the samples were welded with the current intensity of 130, 145 and 160 Ampers by GTAW process and using ER120 SG welding wire with a diameter of 2.4 mm. The metallographic results showed that the microstructure of the weld metal consisted of  lath martensite and acicular ferrite phases, which increased the volume fraction of ferrite from 5 to 32% with the increase of heat input, and the morphology of the ferrite changed from acicular to polygonal ferrite due to the decrease in the cooling rate. The HAZ area microstructure consist of bainite, lath martenrite and ferrite. The highest strength value was obtained in the welded sample with low heat input. With the increase of heat input, the tensile strength has decreased from 1154 to 965 MPa. Also, with the increase of heat input, the impact energy has increased in the welding zone due to the increase of stable phases, and in the HAZ zone due to the growth of the primary austenite grains and the reduction of the grain boundary locking effect. The results of the fracture analysis showed that the fracture occurred in the weld zone with low heat input, brittle fracture, and in the HAZ area, combination of ductil and brittle fracture occurred. With the increase in heat input, dutil fracture occurred in the welding zone and brittle fracture occurred in the HAZ zone due to grain growth.},  
Keywords = {Heat input, Impact energy, Microstructure, D6AC, VCN200 steels},
volume = {10},
Number = {2}, 
pages = {51-61}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {ارزیابی حرارت ورودی برتحولات ریزساختاری و خواص مکانیکی اتصال غیرمشابه فولاد D6AC  به VCN 200 (1.6580) در جوشکاری GTAW},
abstract_fa ={در این تحقیق اثر حرارت ورودی بر ریزساختار و خواص مکانیکی اتصال دو فولاد نامشابهD6AC  و VCN 200 بررسی شد. بدین منظور نمونه‌ها با شدت جریان‌های 130، 145 و 160 آمپر با فرایند GTAW و با استفاده از سیم جوش ER120 SG با قطر 4/2mm جوشکاری شدند. نتایج متالوگرافی نشان داد ریزساختار فلزجوش شامل فازهای مارتنزیت و فریت سوزنی بود که با افزایش حرارت ورودی کسر حجمی فریت از 5 به %32 افزایش و مورفولورژی فریت از سوزنی به فریت چند وجهی بدلیل کاهش نرخ سرمایش تغییر یافته است. منطقه HAZ دارای ریزساختار بینیت، مارتنزیت و فریت بود. بیشترین مقدار استحکام در نمونه جوشکاری شده با حرارت ورودی کم بدست آمد. با افزایش حرارت ورودی استحکام کششی از 1154 بهMPa م965 کاهش یافته است. همچنین با افزایش حرارت ورودی، انرژی ضربه در منطقه‌جوش بدلیل افزایش فازهای پایدار افزایش، و در منطقه HAZ  بدلیل رشد دانه‌های آستنیت اولیه و کاهش اثر قفل‌شوندگی مرز دانه‌ها کاهش یافته است. نتایج حاصل از شکست‌نگاری نشان داد شکست در منطقه جوش با حرارت ورودی کم، شکست ترد، و در منطقه HAZ ترکیبی از شکست نرم و ترد اتفاق افتاده است. با افزایش حرارت وردی در منطقه جوش شکست کاملا نرم و در منطقه HAZ شکست ترد بدلیل رشد دانه رخ داده است.},
keywords_fa = {حرارت ورودی, انرژی ضربه, ریزساختار, فولادهای D6AC, VCN200.},

doi = {10.47176/JWSTI.2025.05},
url = {http://jwsti.iut.ac.ir/article-1-474-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-474-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {Vojdanpak, M. K. and Niroumand, B. and Shamanian, M.},  
title = {Effect of time on transient liquid phase bonding of electron beam melted Ti6242 titanium alloy to AISI 316L stainless steel}, 
abstract ={Despite rapid advancement of additive manufacturing methods in recent years, sufficient research on bonding of additively manufactured materials to conventional alloys has not been conducted. This study evaluates the bonding between austenitic stainless steel L316 and Ti-6242 alloy, fabricated by electron beam melting, using the transient liquid phase (TLP) bonding method. The TLP bonding was achieved using a copper interlayer and processing in a vacuum furnace, examining the effects of process time and surface roughness on bond quality. The samples were characterized by optical and scanning electron microscopy, X-ray diffraction, shear strength testing, and surface roughness measurement. Results showed that reducing the surface roughness increased the shear strength. Additionally, processing time significantly affected the element diffusion, formation of intermetallic compounds like FeTi and TiCu, and the shear strength of the joints. The highest shear strength of 200 MPa was obtained with surface preparation by grinding and polishing and bonding at 980°C for 120 minutes.},  
Keywords = {Additive manufacturing, Transient Liquid Phase bonding, Ti-6Al-2Sn-4Zr-2Mo 316 Stainless steel, Bonding Time, Roughness},
volume = {10},
Number = {2}, 
pages = {63-73}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {تاثیر زمان بر اتصال فاز مایع گذرای آلیاژ تیتانیوم Ti-6242 تولید شده به روش ذوب پرتوی الکترونی به فولاد زنگ‌نزن AISI316L},
abstract_fa ={روش‌های ساخت افزودنی شاهد پیشرفت‌های زیادی در سال‌های اخیر بوده است ولی پژوهش کافی برای اتصال این قطعات با آلیاژهای مرسوم انجام نشده است. مطالعه حاضر برای ارزیابی اتصال بین فولاد زنگ‌نزن آستنیتی 316L و آلیاژ Ti-6242 ساخته شده به روش ذوب پرتوی الکترونی، با استفاده از روش فاز مایع گذرا، انجام شد. اتصال فاز مایع گذرا با استفاده از لایه میانی مس و فراوری در کوره خلاء انجام، و تاثیر زمان فرایند و زبری سطح بر کیفیت اتصال بررسی شد. برای مشخصه‌یابی نمونه‌ها از بررسی‌های ریزساختار نوری و الکترونی روبشی، پراش اشعه ایکس، استحکام برشی و زبری‌سنجی استفاده شد. نتایج نشان داد که با کاهش زبری سطح، استحکام برشی افزایش می‌یابد. همچنین مدت زمان فرایند، تأثیر قابل‌توجهی بر نفوذ عناصر، تشکیل ترکیبات بین‌فلزی مانند FeTi و TiCu و استحکام برشی اتصالات داشت. بالاترین استحکام برشی اتصال برابر با ۲۰۰ مگاپاسکال و در شرایط آماده‌سازی سطح سنباده‌زنی و پولیش شده و اتصال در دما و زمان 980 درجه سانتی‌گراد و 120 دقیقه به دست آمد.},
keywords_fa = {ساخت افزودنی, اتصال فاز مایع گذرا, آلیاژ تیتانیوم 6242, فولاد زنگ نزن 316, زمان اتصال, زبری سطح.},

doi = {10.47176/JWSTI.2025.06},
url = {http://jwsti.iut.ac.ir/article-1-480-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-480-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {Rahimi, M. and Omidi, M. and Jabbarzare, S. and Bakhsheshi-Rad, H. R. and Kasiri-Asgarani, M. and Ghayour, H.},  
title = {Friction stir processing of copper/silver-silicon carbide nanocomposite: microstructure, mechanical and wear properties}, 
abstract ={In this research, copper/silver-silicon carbide Cu-Ag-SiC composite was prepared by the friction stir processing (FSP). For this purpose, nanometer and micrometer SiC particles were used as reinforcing particles. In order to evaluate the microstructural properties, X-ray diffraction (XRD) analysis, scanning electron microscope and optical microscope were employed. Evaluation of mechanical properties through microhardness measurement, tensile test and pin on disc test were utilized to evaluate the wear behavior of the composite. The results of X-ray analysis revealed the presence of two phases of CuAg solid solution along with SiC particles, which indicated the formation of Cu-Ag-SiC composite. The addition of nano-particles led to a significant decrease in the intensity of peaks compared to micro-particles. This indicated a decrease in the grain size of the CuAg matrix. Using the FSP in the presence of reinforcing particles and without it led to a decrease in the crystal size and average grain size compared to the sample without FSP. So that the grain size of the sample without FSP and the FSPed sample without reinforcing particles and with nano-reinforcing particles were found to be about 46.3, 19.2 and 3.6 µm, respectively. The wear mechanism in the sample before FSP was adhesive wear due to its soft nature of the matrix, and after FSP in the sample without reinforcing particles, the adhesive wear decreased and due to the addition of silicon carbide micro and nano- particles reinforcement, the wear mechanism in entirely altered to abrasive wear. Overall, it can be stated that the addition of silicon carbide nanoparticles by FSP leads to the fabrication of  Cu-Ag-SiC composite with high mechanical properties.},  
Keywords = {Friction stir processing, nanocomposite, copper-silver, silicon carbide, microstructure, mechanical properties, wear properties},
volume = {10},
Number = {2}, 
pages = {75-90}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {فرایند اصطکاکی هم‌زدنی نانوکامپوزیت مس-نقره-کاربید سیلیسیم: ریزساختار، خواص مکانیکی و سایشی},
abstract_fa ={در این پژوهش، کامپوزیت مس-نقره-کاربید سیلیسیم با استفاده از فرایند اصطکاکی هم‌زدنی ساخته شد. ذرات تقویت کننده SiC در ابعاد نانو و میکرو استفاده شدند. به منظور ارزیابی خواص ریزساختاری از آنالیز پراش پرتو ایکس، میکروسکوپ الکترونی روبشی و میکروسکوپ نوری استفاده شد. ارزیابی خواص مکانیکی از طریق میکروسختی سنجی، آزمایش کشش و از آزمایش پین بر روی دیسک برای ارزیابی رفتار سایشی کامپوزیت استفاده شد. نتایج آنالیز اشعه ایکس حضور دو فاز زمینه محلول جامد CuAg به همراه ذرات SiC را آشکار کرد که نشان‌دهنده تشکیل کامپوزیت Cu-Ag-SiC بود. این موضوع حاکی از کاهش اندازه دانه زمینه CuAg بود. استفاده از فرایند اصطکاکی هم‌زدنی FSP در حضور ذرات تقویت کننده و بدون آن منجر به کاهش اندازه بلورک و میانگین اندازه دانه نسبت به نمونه بدون FSP شد. به طوری‌که اندازه دانه نمونه بدون FSP و نمونه FSP شده بدون ذرات تقویت کننده و با ذرات تقویت کننده نانو به ترتیب در حدود3/46، 2/19 و 6/3 میکرومتر بدست آمد. کاهش اندازه دانه، ریزتر شدن ذرات تقویت کننده کاربید سیلیسیم از میکرو به نانو و افزایش کسرحجمی ذرات تقویت‌کننده بیشترین تاثیرات را بر میزان سختی گذاشتند به نحوی‌که استفاده از ذرات میکرو در کسر حجمی بیشتر، سختی به بالاترین مقدار خود یعنی 123 ویکرز رسید. سایش در نمونه قبل از FSP به علت ماهیت نرم بودن آن از نوع سایش چسبان و بعد از FSP در نمونه بدون ذرات تقویت کننده سایش چسبان کاهش پیدا کرد و در اثر افزودن ذرات تقویت کننده میکرو و نانومتری کاربید سیلیسیم به طور کلی مکانیزم سایش به خراشان تغییر پیدا کرد. به عنوان یک نتیجه کلی می‌توان بیان نمود که استفاده از ذرات تقویت کننده نانومتری کاربید سیلیسیم بوسیله فرایند اصطکاکی هم زدنی منجر به تولید کامپوزیت  Cu-Ag-SiC با خواص مکانیکی بالا می‌شود.},
keywords_fa = {ساخت افزودنی, اتصال فاز مایع گذرا, آلیاژ تیتانیوم 6242, فولاد زنگ نزن 316, زمان اتصال, زبری سطح.},

doi = {10.47176/JWSTI.2025.07},
url = {http://jwsti.iut.ac.ir/article-1-476-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-476-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {Movahedi, M. and ShiroviKhoozani, H. and Ozlati, A.},  
title = {Effect of friction stir welding process parameters on microstructure and mechanical properties of aluminum/polypropylene joint}, 
abstract ={In this research, the influence of friction stir welding parameters (tool traverse speed ranging from 50 to 150 mm/min, and tool rotational speed ranging from 300 to 1100 rpm) was investigated on the microstructure and mechanical properties of AA5052 aluminum/PP-Z30S polypropylene joint. Results showed that joint formation was accompanied by the formation of mechanical locks in the shape of anchor-like aluminum pieces. Decreasing the heat input (either by increasing the tool traverse speed or decreasing the tool rotational speed) resulted in the formation of larger anchors. The results of tensile-shear test showed that increasing the tool traverse speed from 50 to 100 mm/min led to an enhancement in the fracture load (by ~10%), while at higher traverse speeds, the fracture load decreased (from 235 to 181 N) due to the formation of defects and voids at the joint interface. An increase in the tool rotational speed from 300 to 900 rpm resulted in a superior fracture load (by 70%) due to the formation of anchors perpendicular to the polymer surface with greater penetration depth.},  
Keywords = {Friction Stir Welding, AA5052 Aluminum, PP-Z30S Polypropylene, Mechanical locks, Microstructure, Mechanical properties.},
volume = {10},
Number = {2}, 
pages = {91-102}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {اثر متغیرهای فرایند جوشکاری اصطکاکی تلاطمی بر ریزساختار و خواص مکانیکی اتصال آلومینیوم/پلی‌پروپیلن},
abstract_fa ={در این پژوهش، اثر متغیرهای فرایند جوشکاری اصطکاکی تلاطمی (سرعت انتقالی ابزار در بازه‌ 50 تا 150 میلی‌متر بر دقیقه و سرعت چرخشی ابزار در بازه‌ 300 تا 1100 دور بر دقیقه) بر ریزساختار و خواص مکانیکی اتصال آلومینیوم AA5052 به پلی‌پروپیلن PP-Z30S مورد مطالعه قرار گرفت. بررسی‌های ریزساختاری با میکروسکوپ‌های نوری و الکترونی روبشی نشان داد ایجاد اتصال با تشکیل قفل‌های مکانیکی به شکل قطعات لنگر مانندی از جنس آلومینیوم همراه است. به‌علاوه مشاهده شد که کاهش حرارت ورودی (با افزایش سرعت خطی و یا کاهش سرعت چرخشی ابزار) موجب افزایش اندازه‌ این لنگرها می‌شود. نتایج آزمون کشش-برش نشان داد که افزایش سرعت انتقالی ابزار از 50 به 100 میلی‌متر بر دقیقه با افزایش اندازه‌ لنگرها موجب افزایش نیروی شکست (حدود %10) می‌شود. اگرچه، افزایش بیشتر سرعت چرخشی، بدلیل ایجاد عیوب و حفرات در فصل مشترک اتصال، نیروی شکست را کاهش داد (از 235 به 181 نیوتن). افزایش سرعت چرخشی از 300 تا 900 دور بر دقیقه نیز با ایجاد لنگرهای عمود بر سطح پلیمر و با عمق نفوذ بیشتر، موجب افزایش استحکام اتصال (تا حدود %70) شد.},
keywords_fa = {جوشکاری اصطکاکی تلاطمی, آلومینیوم AA5052, پلی‌پروپیلن PP-Z30S, قفل مکانیکی, ریزساختار, خواص مکانیکی.},

doi = {10.47176/JWSTI.2025.08},
url = {http://jwsti.iut.ac.ir/article-1-464-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-464-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {Shahin, F. and Baharzadeh, E. and Rafiei, M. and Mostaan, H.},  
title = {The effect of Cr addition on microstructure and tribological properties of iron aluminide cladding produced by GTAW process}, 
abstract ={In this study, formation of Fe3Al and (Fe,Cr)3Al intermetallic compounds and the effect of Cr on microstructural and mechanical properties of Fe-Al cladding system such as hardness and wear resistance, were evaluated. For this purpose, first, iron and aluminum powders were mixed in the first series without chromium powder and in the second series with the addition of chromium powder in high energy planetary ball mill, and Fe3Al and (Fe,Cr)3Al intermetallic compounds were synthesized. The preplaced powders were cladded on the surface of CK45 steel using gas tungsten arc welding process. The microstructure, formed phases and properties of the cladded layers were studied by optical microscope, scanning electron microscope, X-Ray Diffraction, micro and macro hardness, energy dispersive X-ray spectroscopy (EDS) and pin on disk wear test at 25, 250, and 500ᵒC temperatures. It was found that the microstructure of Fe-Al binary cladding contained Fe3Al dendrites with non-epitaxial growth. This non-epitaxial growth results from the difference in the chemical composition of the coating and the substrate at the interface between the coating and the substrate, which has caused the formation of new crystals at the interface. However, the microstructure of Fe-Al-Cr ternary cladding contained martensitic blades within (Fe,Cr)3Al matrix. The results of hardness tests revealed that the hardness of ternary cladding is twice as compared with the binary cladding (30 and 60 HRC for binary and ternary claddings, respectively). Also it was found that the presence of Cr element in Fe-Al cladding improved the wear resistance of deposited layers. The predominant wear mechanism of Fe3Al pin was adhesive, while for (Fe,Cr)3Al pin moreover adhesive wear, micro-plowing abrasive wear was also seen. The mass losses of both pins were maximum at ambient temperature and minimum at temperature of 500 oC.},  
Keywords = {GTAW, Fe3Al, (Fe,Cr)3Al, Cladding, Hardness, Wear},
volume = {10},
Number = {2}, 
pages = {103-119}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {تاثیر افزودن کروم بر ریزساختار و خواص تریبولوژیکی روکش آلومیناید آهن تولید شده توسط فرایند GTAW},
abstract_fa ={در این مطالعه، تشکیل ترکیبات بین‌فلزی Fe3Al و Fe,Cr3)Al ) و تأثیر کروم بر ریزساختار و خواص مکانیکی روکش دوتایی Fe-Al از جمله سختی و مقاومت در برابر سایش، مورد بررسی قرار گرفت. برای این منظور، ابتدا پودرهای آهن و آلومینیوم در مرحله اول بدون پودر کروم و در مرحله دوم با افزودن پودر کروم در آسیاب سیاره‌ای با انرژی بالا مخلوط و ترکیبات بین‌فلزی Fe3Al و Fe,Cr3)Al ) سنتز شدند. پودرهای از پیش قرار داده شده بر سطح فولاد CK45 با استفاده از فرایند جوشکاری قوس تنگستن گاز، روکش‌کاری شدند. ریزساختار، فازهای تشکیل شده و خواص لایه‌های روکش ایجاد شده با استفاده از میکروسکوپ نوری، میکروسکوپ الکترونی روبشی، آنالیز پراش پرتو ایکس، سختی‌سنجی میکرو و ماکرو، طیف‌سنجی توزیع انرژی پرتو ایکس و آزمایش سایش پین روی دیسک در سه دمای 25، 200 و 500 درجه سانتی‌گراد بررسی شدند. نتایج نشان داد که ریزساختار روکش دوتایی Fe-Al شامل دندریت‌های Fe3Al با رشد غیراپیتاکسیال است. این رشد غیراپیتکسیال نتیجه تفاوت ترکیب شیمیایی پوشش و زیرلایه در فصل مشترک پوشش و زیرلایه است که باعث شکل‌گیری کریستال‌های جدید در فصل مشترک شده است. این درحالی است که ریزساختار روکش سه‌تایی Fe-Al-Cr شامل تیغه‌های مارتنزیتی درون زمینه Fe,Cr3)Al ) می‌باشد. نتایج آزمایش‌های سختی نشان داد که سختی روکش سه‌تایی دو برابر روکش دوتایی (به‌ترتیب30 و 60راکول‌سی برای روکش‌‌های دوتایی و سه‌تایی) است. همچنین مشخص شد که حضور عنصر کروم در روکش Fe-Al مقاومت در برابر سایش لایه‌های رسوبی را بهبود می‌بخشد. مکانیسم سایش غالب در پین Fe3Al سایش چسبان بود، در حالی‌که برای پین Fe,Cr3)Al ) علاوه بر سایش چسبان، سایش خراشان ریزشخم نیز مشاهده شد. میزان کاهش وزن هر دو پین در دمای محیط حداکثر و در دمای 500 درجه سانتی‌گراد حداقل بود.},
keywords_fa = {GTAW, Fe3Al, (Fe,Cr)3Al, روکش‌کاری, سختی, سایش.},

doi = {10.47176/JWSTI.2025.09},
url = {http://jwsti.iut.ac.ir/article-1-472-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-472-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {AbediChermahini, H. and Atapoor, M. and Esmailzadeh, M.},  
title = {Microstructural and corrosion evaluation of AH36 low-alloy steel cladded with nickel and copper alloy filler wires using GTAW}, 
abstract ={Nowadays, in order to achieve the combined properties of multiple alloys for important applications such as automotive and marine industries, the use of cladding method is common. Cladding, which is a type of coating through welding, is one of the widely used methods for surface modification of metal parts and sheets in industry. AH36 low-alloy steel is a steel used in shipbuilding, known for its toughness and good corrosion resistance, making it a significant condidcate among other steels used in this industry. In this research, to enhance the corrosion properties of AH36 steel, the cladding process was performed using Gas Tungsten Arc Welding (GTAW) with copper/nickel filler wire. Two samples, one from the coated (weld metal) and one from the uncoated (base metal) sections, were prepared and subjected to microstructural and corrosion investigations. The results indicated an increase in grain size in the heat-affected zone of the weld metal sample, leading to a reduction in mechanical properties. The cyclic polarization test showed that the base metal had higher susceptibility to pitting corrosion compared to the weld metal. Additionally, the weld metal exhibited a higher tendency for repassivation or repairing of the pits. The results of the electrochemical impedance spectroscopy (EIS) test indicated that both the base metal and weld metal samples had a single-loop equivalent circuit. The larger diameter of the Nyquist semicircle for the base metal compared to the weld metal suggests better uniform corrosion behavior of the base metal relative to the weld metal.},  
Keywords = {Low-Alloy Steel, AH36, Shipbuilding Steel, Nickel/Copper},
volume = {10},
Number = {2}, 
pages = {121-130}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {بررسی ریزساختار و رفتار خوردگی فولاد کم‌آلیاژ (AH36) روکش‌کاری شده به روش جوشکاری قوسی تنگستن (GTAW) با سیم جوش از جنس نیکل و مس},
abstract_fa ={امروزه در دنیا به منظور دستیابی هم‌زمان به خواص چند آلیاژ متفاوت در کاربردهای مهم نظیر خودروسازی و دریایی، استفاده از روش روکش‌کاری سطح مرسوم است. پوشش‌دهی به روش جوشکاری (روکش‌کاری) یکی ازروش‌های پراستفاده در اصلاح سطح قطعات و ورق‌های فلزی در صنعت است. فولاد کم‌آلیاژ  AH36 یک از فولادهای مورد استفاده در صنعت کشتی‌سازی به شمار می‌رود که به جهت چقرمگی و مقاومت به خوردگی خوب، شهرت فراوانی در بین سایر فولادهای مورد استفاده در این صنعت پیدا کرده است. در این تحقیق به‌منظور بهبود خواص خوردگی این فولاد، فرایند روکش‌کاری به روش جوشکاری قوسی تنگستن با گاز محافظ با استفاده از سیم‌جوش از جنس مس/نیکل انجام شد. سپس دو نمونه از قسمت‌های با و بدون روکش تحت عنوان فلزپایه و فلزجوش تهیه شده و مورد بررسی‌های ریزساختاری و خوردگی قرار گرفت. نتایج حاصل حاکی از افزایش اندازه دانه در منطقه متأثر از حرارت نمونه  فلزجوش و به دنبال آن کاهش خواص مکانیکی بود. آزمون پلاریزاسیون سیکلی نشان داد که فلز پایه حساسیت بالاتری به خوردگی حفره‌ای نسبت به فلز جوش دارد. همچنین، فلزجوش تمایل بالاتری برای ترمیم مجدد حفرات از خود نشان داد. نتایج آزمون امپدانس الکتروشیمیایی الکتروشیمیایی نشان داد که نمونه فلزپایه و فلزجوش مدار معادل تک حلقه‌ای دارند. قطر حلقه نایکوییست بزرگتر فلزپایه نسبت به فلزجوش نشان‌دهنده رفتار بهتر خوردگی یکنواخت فلزپایه نسبت به فلزجوش بود.},
keywords_fa = {فولاد کم‌آلیاژ, AH36, فولاد کشتی, نیکل/مس.},

doi = {10.47176/JWSTI.2025.10},
url = {http://jwsti.iut.ac.ir/article-1-478-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-478-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {Ranjbar, Kh. and Firoozi, A. and ShahriariNogoorani, F. and Ziaee, S. F.},  
title = {Overlaying of colmonoy 6 on plain carbon steel by plasma transfer arc welding and tungsten inert gas welding: comparison of microstructure and wear behavior}, 
abstract ={Plain carbon steels are widely utilized in various industrial applications primarily due to their low cost. However, these steels often fall short in terms of mechanical properties and wear resistance. The deposition of hard and wear-resistant coatings on these steels significantly enhances their performance and extends their range of applications. Colomonoy 6, is a nickel-based superalloy, enhance hardness, erosion resistance, wear resistance, and corrosion resistance on the applied surfaces. The study investigated the application of weld overlay using colomonoy 6 on a plain carbon steel, aimed to create a hard and wear-resistant surface. The overlaying processes were performed using plasma transfer arc welding and gas tungsten arc welding under identical conditions. Microstructural characteristics were examined through optical and electron microscopy, and Phase analysis was performed using X-ray diffraction technique. The wear behavior of the weld overlays was evaluated using pin-on-disc wear testing at three different temperatures: 25 °C, 300 °C, and 600 °C, using an alumina pin. The microstructural investigation revealed the formation of dendritic nickel-rich solid solutions and interdendritic carbide and boride phases within the overlays, contributing to improved hardness and wear properties. Results demonstrated that in both overlaying methods, the wear mechanism at room temperature was mild abrasive, whereas at 600 °C, it was plastic deformation, exhibiting a wear track depth of approximately 33-35 μm, and 50-55 μm, respectively. In both overlayed metals, an approximate Vickers hardness number of 600 was measured a 4-fold increase in hardness of substrate. This finding suggests that factors other than hardness, such as microstructural stability and phase distribution at elevated temperatures, play significant roles in wear performance.},  
Keywords = {Overlaying, Colomonoy 6, Plasma transfer arc welding, Gas tungsten arc welding,  Wear behavior, Boride and carbide phases.},
volume = {10},
Number = {2}, 
pages = {131-142}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {روکش‌کاری کلمونوی ۶ بر روی فولاد ساده کربنی با جوشکاری قوس انتقالی پلاسما و قوس تنگستن: مقایسه ریز ساختار و خواص سایشی},
abstract_fa ={فولادهای ساده کربنی با توجه به ارزان بودن آن‌ها کاربردهای مختلفی در صنعت دارند ولی خواص مکانیکی و مقاومت سایشی مطلوبی ندارند. اعمال پوشش‌های سخت و مقاوم به سایش کارایی و حوضه کاربرد آن‌ها را افزایش می‌دهد. پوشش کلمونوی۶ (Colmonoy6) از جنس سوپر آلیاژهای پایه نیکل می‌باشد که باعث افزایش سختی و مقاومت در برابر سایش، فرسایش و خوردگی سطح می‌شود. هدف این پژوهش بررسی خواص سایشی روکش سخت و مقاوم به سایش کلمونوی۶ بر روی زیرلایه فولاد ساده کربنی می‌باشد. در این تحقیق روکش کلمونوی۶با استفاده از فرایند جوشکاری به دو روش قوس انتقالی پلاسما وقوس تنگستن و در شرایط یکسان انجام شد. خصوصیات ریزساختاری و رفتار سایشی نمونه‌ها در دماهای مختلف باهم مقایسه شدند. بررسی‌های ریزساختاری توسط میکروسکوپ‌های نوری و الکترونی، و آنالیزهای فازی توسط آنالیز پراش پرتو ایکس صورت گرفت. آزمون سایش پین بر روی دیسک در سه دمای ۲۵، ۳۰۰ و ۶۰۰ درجه سانتی‌گراد و با استفاده از پین سرامیکی آلومینایی انجام شد. بررسی‌های ریزساختاری روکش، تشکیل محلول جامد غنی از نیکل دندریتی، وترکیبات بورایدی و کاربیدی بین دندریتی در روکش‌ها که موجب افزایش سختی و بهبود مقاومت سایشی می‌شوند را تایید کردند. نتایج نشان داد که در هر دو روش روکش‌کاری، مکانیزم سایش در دمای اتاق از نوع سایش خراشان ملایم، در حالی‌که در دمای ۶۰۰ درجه، مکانیزم سایش از نوع تغییر شکل پلاستیکی است که بترتیب دارای عمق شیار سایشی در حدود ۳5-۳3 میکرون، و ۵5-۵0 میکرون می باشند. در هر دو روش، سختی روکش تقریبا عدد ۶۰۰ ویکرز را نشان داد که افزایش چند برابری نسبت به زیرلایه دارد. یافته‌های این پژوهش نشان می‌دهد که عواملی به غیر از سختی در تعیین رفتار سایشی نقش بازی می‌کنند که از آن جمله می‌توان به پایداری ریزساختاری و توزیع فازها در دمای بالا اشاره کرد.},
keywords_fa = {روکش‌کاری, کلمونوی6, جوشکاری قوس انتقالی پلاسما, جوشکاری قوس تنگستن, رفتار سایش, ترکیبات بورایدی و کاربیدی.},

doi = {10.47176/JWSTI.2025.11},
url = {http://jwsti.iut.ac.ir/article-1-481-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-481-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}

@article{ 
author = {Ranjbarnodeh, E. and Raissi, P. and Kolagar, A. and Cheraghzadeh, M.},  
title = {Dissolution kinetics of γ′ precipitate in IN738LC nickel base superalloy using arc heat treatment}, 
abstract ={Nickel base superalloy IN738LC is widely used in power plant industry and gas turbine blade manufacturing. The main strengthening mechanism of this alloy is the precipitation hardness caused by γ′ precipitates. These precipitates play an important role in determining the mechanical properties of this alloy and their amount and morphology changes under heat treatment. In this research, in order to investigate the evolution of γ' precipitates during heat treatment, a number of solution annealed samples were subjected to arc heat treatment. In this heat treatment, by applying heat caused by a static arc, a temperature ranges from the ambient temperature to above the melting point is created in the sample. Using this process, samples with 100 amp currents were heat treated for 1, 2 and 15 minutes. Electron microscope, image processing and transient heat transfer model with axial symmetry were used for experimental and mathematical investigations. In the following, using the experimental and numerical results simultaneously, a mathematical model for the dissolution kinetics of γ' precipitates in the heat-affected zone of these welds was presented. The results of electron microscopy showed that the dissolution rate and shape of γ′ precipitates are strongly influenced by the distance from the heat source. The activation energy of dissolution of γ′ precipitates increased with increasing time and its value was between 40 and 80 kJ/mol.},  
Keywords = {Superalloy IN738LC, arc heat treatment, dissolution kinetics of γ′, finite element model.},
volume = {10},
Number = {2}, 
pages = {143-155}, 
publisher = {Iranian Institute of Welding and Non Destructive Testing},
title_fa = {سینتیک انحلال رسوبγ\' در سوپرآلیاژ پایه نیکل IN738LC  با استفاده از عملیات حرارتی قوسی},
abstract_fa ={سوپرآلیاژ پایه نیکل IN738LC به طور گسترده در صنایع نیروگاهی و ساخت پره توربین گاز مورد استفاده قرار می‏گیرد. مکانیزم اصلی استحکام‏دهی این آلیاژ رسوب سختی ناشی از رسوبات γ '  است. این رسوبات نقش مهمی در تعیین خواص مکانیکی این آلیاژ دارند و تحت عملیات حرارتی، میزان و مورفولوژی آن‌ها دچار تغییر می‏شود. در این پژوهش، جهت بررسی نحوه تکامل رسوبات γ '  حین عملیات حرارتی، تعدادی نمونه‏‌های آنیل محلولی شده، تحت عملیات حرارتی قوسی قرار گرفتند. در این عملیات حرارتی با استفاده از اعمال حرارت ناشی از قوس ساکن، محدوده دمایی از دمای محیط تا بالای نقطه ذوب در نمونه ایجاد می‌شود. با استفاده از این فرایند، نمونه‏‌هایی با شدت جریان‌های 100 آمپر به مدت ‌زمان 1 و 2 و 15 دقیقه عملیات حرارتی شدند. برای بررسی‌های تجربی و ریاضی از میکروسکوپ الکترونی، پردازش تصویر و مدل انتقال حرارت گذرا با تقارن محوری استفاده شد. در ادامه با استفاده هم‌زمان از نتایج تجربی و عددی، یک مدل ریاضی برای سینتیک انحلال رسوبات γ ' در منطقه متأثر از حرارت این جوش‌ها ارائه شد. نتایج میکروسکوپ الکترونی نشان دادند که میزان انحلال و شکل رسوبات γ '  به شدت تحت تأثیر فاصله از منبع حرارتی است. میزان انرژی اکتیواسیون انحلال رسوبات γ '  با افزایش زمان، افزایشی بوده و مقدار آن نیز بین 40 تا 80 کیلوژول بر مول به دست آمد.},
keywords_fa = {سوپرآلیاژIN738LC , عملیات حرارتی قوسی, سینتیک انحلال رسوب′γ, مدل المان محدود.},

doi = {10.47176/JWSTI.2025.12},
url = {http://jwsti.iut.ac.ir/article-1-482-en.html},  
eprint = {http://jwsti.iut.ac.ir/article-1-482-en.pdf},  
journal = {Journal of Welding Science and Technology of Iran},  
issn = {2476-583X}, 
eissn = {2676-6787}, 
year = {2024}  
}