fa تاثیر درصد هم پوشانی تک پاس های روکش بر ریز ساختار و خواص مکانیکی روکش کاری با لیزر پودر اینکونل625 بر روی فولاد ASTM A592 <span style="color:black;"><span style="font-family:B Lotus;"><span style="font-size:11.0pt;">در این تحقیق اثر درصد هم پوشانی تک پاس های روکش بر روی ریزساختار و خواص مکانیکی روکش کاری با لیزر پودر اینکونل625 بر روی فولاد کوئنچ و تمپر </span></span></span><span dir="LTR"><span style="color:black;"><span style="font-size:9.0pt;">ASTM A592</span></span></span><span style="color:black;"><span style="font-family:B Lotus;"><span style="font-size:11.0pt;"> مورد بررسی قرار گرفت. جهت آنالیز ساختاری، فاصله بین دندریتی ارزیابی شد و برای این منظور از میکروسکوپ الکترونی روبشی و نرم افزار </span></span></span><span dir="LTR"><span style="color:black;"><span style="font-size:9.0pt;">Digimizer</span></span></span><span style="color:black;"><span style="font-family:B Lotus;"><span style="font-size:11.0pt;"> استفاده گردید. جهت بررسی خواص مکانیکی، مدول الاستیک، چقرمگی و ریز سختی مورد ارزیابی قرار گرفت. در ارزیابی مدول الاستیک از روش فرو رونده نوپ و در ارزیابی چقرمگی از روش ایوانز استفاده شد. بعد از بررسی های انجام شده مشخص گردید که در هم پوشانی&nbsp; تک پاس های روکش 50 درصد، میزان حرارت ورودی کم تر از هم پوشانی تک پاس های روکش 75 درصد است، همچنین دارای ساختار ریزتر و خواص مکانیکی به مراتب بالاتری می باشد به طوری که فاصله بین دندریتی در هم پوشانی تک پاس های روکش 50 درصد، حدود 91/. میکرومتر، قطر میانگین ستون های دندریتی حدود 32/. میکرومتر، ریزسختی حدود 10 درصد، سختی نوپ حدود 9 واحد، مدول الاستیک حدود 37 گیگا پاسکال و چقرمگی حدود 9 مگاپاسکال در مجذور متر از هم پوشانی 75 درصد بیشتر است.</span></span></span><span style="font-family:B Lotus;"><span style="font-size:6.0pt;"></span></span> In this study, the effect of overlapping percentage on microstructure and mechanical properties of a single-pass coating by Inconel 625 powder laser has been investigated for quench-tempered ASTM A592 steel. In order to have a structural analysis, the inter dendritic distance was evaluated. For this purpose, scanning electron microscopy (FESEM) and Digimizer software were adopted. In order to investigate mechanical properties, elastic modulus, toughness, and micro hardness were evaluated. For the evaluation of elastic modulus, Noop indentation method was used, and for toughness studies, Evans method was applied. After the investigation, it was found that in the overlapping of single-pass 50% coatings, the heat input value is lower than overlapping in single-pass 75% coatings. It also contains a finer structure with much higher mechanical properties. This is in such a way that the inter dendritic distance in single-pass 50% coatings is about 0.91 &micro;m. The average diameter of the dendritic columns is about 0.32 &micro;m, hardness value is about 10%, Knoop hardness is about 9 units, elastic modulus is about 37 GPa, and toughness is about 9 MPa m1/2 higher in comparison with the 75% overlapping case<strong>.</strong> روکش کاری با لیزر, اینکونل 625, فولاد A592, ریزساختار, خواص مکانیکی. Laser cladding, Inconel 625, A592 steel, Microstructure, Mechanical properties 147 156 http://jwsti.iut.ac.ir/browse.php?a_code=A-10-190-14&slc_lang=fa&sid=1 P. Shayanfar پیمان شایان فر Yes Department of Materials Science and Engineering, School of Engineering, Shiraz University, Shiraz, Iran دانشکده مهندسی مواد، دانشکده مهندسی، دانشگاه شیراز. H. Daneshmanesh حبیب دانش منش No Department of Materials Science and Engineering, School of Engineering, Shiraz University, Shiraz, Iran دانشکده مهندسی مواد، دانشکده مهندسی، دانشگاه شیراز. K. Janghorban کمال جانقربان No Department of Materials Science and Engineering, School of Engineering, Shiraz University, Shiraz, Iran دانشکده مهندسی مواد، دانشکده مهندسی، دانشگاه شیراز.