TY - JOUR JF - JWSTI JO - JWSTI VL - 4 IS - 2 PY - 2019 Y1 - 2019/1/01 TI - Development of dissimilar GTA 4130/201 SS weld joint and investigation on the effect of filler metals in order to obtain improved mechanical properties and microstructural features TT - توسعه اتصالات ذوبی غیرمشابه فولاد 4130 به فولاد زنگ نزن آستنیتی 201 و بررسی اثر فلزات پرکننده مختلف با هدف دستیابی به خواص مکانیکی و مشخصه‌های ریزساختاری بهبود یافته با استفاده از روش قوسی تنگستن-گاز N2 - In this research, gas tungsten arc welding of dissimilar joint between 4130 low alloy steel and AISI 201 austenitic stainless steel was investigated. Four filler metals i. e. ERNiCr-3, ER 309L, ER 308L and ER 80SB2 were used. After welding, microstructural features of various areas and also fracture surfaces were examined using optical microscopy and scanning electron microscopy. Tensile test was conducted in order to study the mechanical properties of each joint. It was found that ERNiCr-3 is fractured from fusion zone and the others were fractured from 4130 base metal. Also, some second phase particles such as NbC were seen in the ERNiCr-3 weld joint. SEM observation showed that the fracture behavior of ERNiCr-3 weld joint is semi brittle and the others are ductile. The fusion zone of ERNiCr-3 weld joint was fully austenitic and consisted of equiaxed grains and no crack was seen in this area. The fusion zone of ER 308L and ER 309L were composed from cellular dendrite and finally ER 80S-B2 weld joint was consisted of lath martensite. SP - 1 EP - 12 AU - Gholami, M. AU - Mostaan, H. AU - Sonboli, A. AD - KW - Dissimilar joints KW - Gas tungsten arc welding KW - AISI 201 austenitic stainless steel KW - AISI 4130 low alloy steel KW - Mechanical properties KW - Microstructure UR - http://jwsti.iut.ac.ir/article-1-221-en.html ER -