Volume 4, Issue 2 (Journal OF Welding Science and Technology of Iran 2019)                   JWSTI 2019, 4(2): 87-98 | Back to browse issues page

XML Persian Abstract Print


1- Faculty of Engineering, Mahallat Institute of Higher Education, Mahallat, Iran.
2- Faculty of Engineering, Islamic Azad University of Arak, Arak, Iran
Abstract:   (5319 Views)
High strength low alloy steels are widely used in gas industry, so shield metal arc welding in pipelines to transport natural gas from Iran is of great importance. For experimental investigation of seam weld and integrity of girth weld, destructive and non-destructive tests are required. In this article the effects of normal heat treatment on properties of multi pass welding in different situations (6-7:30 , 7:30-9 , 9-10:30 , 10:30-12) with 36 in outside diameter is evaluated by chemical,  metallography, tensile, toughness and hardness. The result shows that normalizing increases ferrite ratio in root pass and weld cap pass respectively 24 and 6 percent than base steel. Also the increase rate of ferrite in root, hot, filler, and the cap pass are respectively 32, 14, 12 and 7 percent before than normalizing. The elongation weld of was increased ratio than before the heat treatment in base metal respectively 65 and 5 percent. The impact energy alignment to weld (9-10:30) had a rate of 70 percent increase before the heat treatment. The increase rate of C, V and Ti in the weld zone according to base metal in situation of 6-7:30 are respectively 0.01, 0.003 and 0.005.
Full-Text [PDF 5977 kb]   (1091 Downloads)    
Type of Study: Research | Subject: Special

Rights and permissions
Creative Commons License This work is licensed under a Creative Commons Attribution-NonCommercial 4.0 International License.